The aim of this study was to investigate and understand bacterial adhesion to different dental material surfaces like amalgam, Chromasit, an Co-Cr alloy, an IPS InLine ceramic, yttrium stabilized tetragonal polycrystalline zirconia (TPZ), a resin-based composite, an Au-Pt alloy, and a tooth. For all materials, the surface roughness was assessed by profilometry, the surface hydrophobicity was determined by tensiometry, and the zeta potential was measured by electrokinetic phenomena. The arithmetic average roughness was the lowest for the TPZ ceramic (R_a = 0.23 µm ± 0.02 µm), while the highest value was observed for the Au-Pt alloy (R_a = 0.356 µm ± 0.075 µm). The hydrophobicity was the lowest on the TPZ ceramic and the highest on the Co-Cr alloy. All measured streaming potentials were negative. The most important cause of tooth caries is the bacterium Streptococcus mutans, which was chosen for this study. The bacterial adhesion to all material surfaces was determined by scanning electron microscopy. We showed that the lowest bacterial extent was on the amalgam, whereas the greatest extent was on tooth surfaces. In general, measurements showed that surface properties like roughness, hydrophobicity and charge have a significant influence on bacterial adhesion extent. Therefore, dental material development should focus on improving surface characteristics to reduce the risk of secondary caries.

Bacterial adhesion can be controlled by different material surface properties, such as surface charge, on which we concentrate in our study. We use a silica surface on which poly(allylamine hydrochloride)/sodium poly(4-styrenesulfonate) (PAH/PSS) polyelectrolyte multilayers were formed. The corresponding surface roughness and hydrophobicity were determined by atomic force microscopy and tensiometry. The surface charge was examined by the zeta potential measurements of silica particles covered with polyelectrolyte multilayers, whereby ionic strength and polyelectrolyte concentrations significantly influenced the build-up process. For adhesion experiments, we used the bacterium Pseudomonas aeruginosa. The extent of adhered bacteria on the surface was determined by scanning electron microscopy. The results showed that the extent of adhered bacteria mostly depends on the type of terminating polyelectrolyte layer, since relatively low differences in surface roughness and hydrophobicity were obtained. In the case of polyelectrolyte multilayers terminating with a positively charged layer, bacterial adhesion was more pronounced than in the case when the polyelectrolyte layer was negatively charged.

The sensitivity of two commercial metal oxide (MOx) sensors to ethylene is tested at different relative humidities. One sensor (MiCS-5914) is based on tungsten oxide, the other (MQ-3) on tin oxide. Both sensors were found to be sensitive to ethylene concentrations down to 10 ppm. Both sensors have significant response times; however, the tungsten sensor is the faster one. Sensor models are developed that predict the concentration of ethylene given the sensor output and the relative humidity. The MQ-3 sensor model achieves an accuracy of ±9.2 ppm and the MiCS-5914 sensor model predicts concentration to ±7.0 ppm. Both sensors are more accurate for concentrations below 50 ppm, achieving ±6.7 ppm (MQ-3) and 5.7 ppm (MiCS-5914).

This work reports on inkjet- and 3D-printed force/pressure sensing devices. The employed printing processes can enable cost- and resource-efficient, fast and flexible designs compared to solid-state technology which is used as a reference design. The pressure sensing devices are realized as either 3D-printed steel or 3D-printed ceramic diaphragms. Both designs thus withstand harsh environmental conditions and elevated temperatures. Additionally, the increased size guarantees less sensitivity to dirt or moisture due to the larger diameter of the diaphragms. The hardware used for the capacitive sensor read-out is based on a shunt measurement system and subsequent demodulation. This architecture enables long cabling, allowing for large parasitic capacitances, without significant loss of transferred signal power, due to the employed power matching to the transmission line. Physical analyses such as contact angle measurements, profilometer measurements, and focused ion beam analysis are done to characterize the resulting printed surfaces. Then, the response of both designs is evaluated by applying force on the diaphragms surface using a moveable load cell. The gathered results are also compared to finite element method simulations.

Restorations in dentistry must reproduce the aspect of the patient’s natural teeth and require non-toxicity, biocompatibility, and good mechanical properties in order to last longer. Restorations are permanently in contact with microbes that can adhere to and form biofilms. The purpose of this study was to determine the adhesion extent of Streptococcus mutans to polymethyl methacrylate (PMMA) resin base containing TiO₂ nanoparticles. To understand the adhesion of Streptococcus mutans on the modified resin-based surfaces, the following surface properties were measured: the roughness, contact angle, zeta potential and CIE color parameters. Evaluation of tensile stress performance in TiO2 modified PMMA showed that the maximum tensile stress of the modified PMMA resin decreases with an increasing amount of TiO₂ nanoparticles. The increasing amount of TiO₂ decreases the roughness and causes contact angles in the border between hydrophilic and hydrophobic surfaces. All the studied surfaces are negatively charged and added TiO₂ tends to increase the zeta potential. The addition of TiO₂ nanoparticles increases the lightness and decreases the intensity of the red and yellow color. The increasing addition of TiO₂ nanoparticles into PMMA increases the morphological change of bacterial cells.

Polyelectrolyte multilayers are coatings formed by the alternate deposition of polycations and polyanions on a charged surface. In this study we examined how the type of substrate affects a multilayer prepared from poly(allylamine hydrochloride) and poly(acrylic acid). Silicon and titanium wafers were used as substrates. Their properties were systematically studied using ellipsometry, tensiometry, atomic force microscopy and streaming potential measurements. Multilayers were built up at pH = 7 with tetramethylammonium chloride as the background salt. The growth of films was monitored by ellipsometry, while the morphology and surface roughness were determined by atomic force microscopy. It was found that the thickness of multilayers containing 10 layers on silicon is 10 nm, whereas the thickness of the same film on titanium is three times higher. It was shown that multilayers formed on silicon display a grain-like structure, which was not the case for a film formed on titanium. Such morphological properties are also reflected in the surface roughness. Finally, it was shown that, in addition to the electrostatic interactions, the hydrophobicity of the substrate also plays an important role in the polyelectrolyte multilayer formation process and influences its thickness and properties.