This paper should primarily lead to a targeted expansion of the database dealing with bending characteristics, and thus help to understand the static and dynamic bending strength depending on the direction of external forces. Wood is very often used in the structural elements of buildings and wood products (e.g., furniture), in which there is both a static load, and in many cases a dynamic load, whilst the direction of loading is usually not considered. Specifically, the paper focuses on determining the bending strength and impact strength of seven economically-important wood species in the Czech Republic. The research includes not only the above-mentioned strength characteristics, but also the elastic characteristics, i.e., the static modulus of elasticity, and the dynamic modules of elasticity determined using the ultrasound and resonance methods. The procedure was methodologically in accordance with the valid harmonized standards or the usual methodological regulations. The most significant finding can be considered that the largest difference of the mean values of impact strength in the radial direction to the tangential direction was recorded for spruce wood, namely 50.3%. Slightly smaller differences were observed for larch wood, i.e., 41.2%. Minor differences of around 20% were recorded for beech, ash and oak wood. A difference with the opposite trend was recorded for birch wood rather than for the above-mentioned woods, namely −9.5%. Linden wood showed almost no difference (−0.8%). With regard to static bending strength, it was found that the largest difference (radial/tangential) was recorded for oak wood, i.e., 7.9%, while smaller differences were found for linden wood amounting to 6.6% and birch 4.7%. For spruce, larch, beech and ash wood, these differences are negligible. Another finding is that the dynamic modules of elasticity are greatly overestimated compared to static modules of elasticity. In the case of the examined wood of coniferous trees, these differences were up to a maximum of 20%. For wood of wood species with a diffuse-porous structure of wood, the differences were more pronounced, i.e., the range of 36% to 68%, and for wood species with a ring-porous structure in the range of 21% to 43%.

The effect of the initial modification of beech and spruce wood using a solution of caffeine and of a commercial product FN-NANO^® FN-1 containing a water dispersion of TiO₂ nanoparticles for increasing the service life of a transparent oil and acrylate coatings during 6 weeks of artificial accelerated weathering was tested. Changes in colour, gloss, and the contact angle of water were monitored. Degradation of the coating film was also evaluated visually and microscopically. The resistance of the coatings to mould growth was also subsequently tested. Based on the results, it is possible to recommend the initial treatment of spruce and beech wood with a 2% caffeine solution or 15% solution of FN-NANO^® dispersion to increase the overall life of a transparent acrylic coating in exterior applications. No positive effect of the applied treatments was observed with the oil coating. In addition, lower concentrations of FN-NANO^® did not have a sufficient effect, and the synergistic effect of using FN-NANO^® in a mixture with a 1% caffeine solution was also not confirmed.

Colour changes and associated wood degradation in exterior and interior applications influenced by ultraviolet (UV) and visible radiation (VIS) decreases the aesthetic value of the products and shortens the overall life of transparent coatings. The aim of the paper is to achieve colour stabilization of oak, larch, Douglas fir and spruce heartwood via surface treatment with UV stabilizers, hindered amine light stabilizers (HALS), nanoparticles TiO₂, ZnO, and mixtures thereof, during exposure to UV and VIS radiation. Colour changes were evaluated during accelerated artificial ageing testing in Xenotest. The distinctly individual character of colour changes in surface treatments due to the underlying wood species was confirmed. A synergistic effect was found when using a combination of active substances compared to substances used individually. The mixture of benzotriazoles with HALS (Tinuvin 5151) in combination with TiO₂ and ZnO nanoparticles was confirmed as one of the most effective treatments for colour stabilization of wood due to UV and VIS spectrums.

This paper focused on the environmental performance of a nearly zero-energy wood-based educational building (NZEB-W) via the life cycle impact assessment (LCIA). It identifies the environmental impacts of construction materials and operational energy demands of the NZEB-W and compares them using the SimaPro 8 software with the IMPACT 2002+ method. The LCIA results from NZEB-W show that the overall environmental impact of construction materials (98.9 Pt) and 45 years operational energy demands (98.6 Pt) will be at the same level. Its overall environmental impact 197.75 Pt for 45 years is relatively small. NZEB-W has the greatest impact on the environment in the category of damage respiratory inorganics (34.5%), 419 kg PM2.5 eq from construction materials, and 271 kg PM2.5 eq from operational energy for 45 years; follows global warming (31.7%), 1.98 × 10⁵ kg CO₂ eq from construction materials, and 4.23 × 10⁵ kg CO₂ eq from operational energy for 45 years; and non-renewable energy (21.8%), 2.82 × 10⁶ MJ primary from construction materials, and 3.73 × 10⁶ MJ primary from operational energy for 45 years. As this environmental assessment shows, the material composition of construction materials compared to the energy consumption in the use phase is an essential element for understanding the life cycle impact of buildings.

Influence of Temperature on the Strength of Bonded Joints

Artificial weathering can significantly reduce the testing time needed for proving coating durability, nevertheless its reliability is still not thoroughly proven. In this study, eight different transparent and pigmented coating systems, namely oil, acrylate, alkyd and urethane alkyd were evaluated through natural and artificial weathering tests on oak samples by measuring colour, gloss and surface wettability and by macroscopic and microscopic evaluation. The oil coatings performed well in wood colour stability evaluations, while the best gloss and wettability change results were noted for acrylate coatings. Pigmented coatings were characterized by significantly lower colour changes than transparent ones. The gloss and wettability changes were more sensitive to coating disruption than to total colour changes of coated wood associated with chemical changes in wood. The findings in this work showed that values of gloss changes and surface wettability for all types of coatings exposed to artificial and natural weathering resulted in significant differences from each other. The data obtained by artificial weathering method provide basic results of coatings durability and, ideally, natural weathering should be performed at the same time to support the results from laboratory tests by exposing wood under real conditions.