Laser welding of copper is characterized by low and unstable light absorption around 1000 nm wavelength. Combination of high thermal conductivity and low melting point makes it difficult to obtain good welding quality and leads to low energy utilization. To improve efficiency and welding quality, a technique to enhance process stability using 1064 nm wavelength Nd:YAG laser has been proposed, and absorption rate and molten volume in laser micro-welding were discussed. Since the surface state of specimen affects absorption phenomena, effects of surface shape and surface roughness were investigated. Absorption rate and molten volume were increased by creating appropriate concave holes and by controlled surface roughness. Stable micro-welding process with deep penetration and good surface quality was achieved for transitional processing condition between heat conduction and keyhole welding, by enhanced absorption rate.

The feasibility of joining laser metal deposited Ti6Al4V sheets using laser beam welding was investigated in this article. The additive manufactured sheets were joined using a 3 kW CW YLS-2000-TR ytterbium laser system. The mechanical properties and microstructure of the welded additive manufactured parts (AM welds) were compared with those of the wrought sheets welded using the same laser process. The welds were characterized and compared in terms of bead geometry, microhardness, tensile strength, fractography, and microstructure. The differences in characteristics are majorly found in the width of the bead and tensile strength. The bead width of AM welds appear wider than the wrought welds, and the wrought welds exhibited higher tensile strength and ductility than the AM welds.

Titanium and its alloys, particularly Ti6Al4V, which is widely utilized in the marine and aerospace industries, have played a vital role in different manufacturing industries. An efficient and cost-effective way of joining this metal is by laser welding. The effect of laser power and welding speed on the tensile, microhardness, and microstructure of Ti6Al4V alloy is investigated in this paper. Results show that the microhardness is highest at the fusion zone and reduces towards the base metal. The microstructure at the fusion zone shows a transformed needle-like lamellar α phase, with a martensitic α’ phase observed within the heat affected zone. Results of tensile tests show an improved tensile strength compared to the base metal.

Titanium alloy Ti6Al4V has been widely applied to medical, automotive, and aerospace industries due to its excellent properties such as high strength and excellent corrosion resistance. On the other hand, additive manufacturing (AM) technology can give the freedom of design of the products. In order to spread the AMed products, the joining of AMed and wrought products are required, and it is important to understand the joint characteristics. In this study, butt welding of Ti6Al4V plate was conducted by fiber laser in argon shielding, and the joint characteristics of laser weld wrought/wrought, AMed/AMed, and AMed/wrought Ti6Al4V plates were experimentally investigated. The AMed plate has higher tensile strength than wrought plate but the elongation of AMed plate is smaller, since AMed plate has α’ martensite due to rapid cooling during laser irradiation in AM process. Then, the laser weld joint of AMed/AMed plates has higher tensile strength, but smaller elongation than that of wrought/wrought plates. The weld joint of AMed/wrought plates shows good welding state, since small heat input leads to formation of small weld bead with higher hardness between wrought and AMed plates.

Titanium and its alloys exhibit a unique combination of mechanical, physical properties and corrosion resistance behaviour which makes them desirable for aerospace, industrial, chemical, medical and energy industries. The selective addition of alloying elements to titanium enables a wide range of physical and mechanical properties to be obtained. Ti-based alloys are finding ever-increasing applications in biomaterials due to their excellent mechanical, physical and biological performance. Intense researches are being pursued in the development of new Ti-based alloys with bio-functionalization closer to human bone, owing to their excellent mechanical strength and resilience when compared to alternative biomaterials, such as polymers and ceramics. Several manufacturing techniques are capable of producing porous materials. There is a need to control pore size, shape, orientation and distribution. This work reviews the application of Ti-based alloys in the biomedical industry and also proposes laser additive manufacture process for the manufacture of medical implants.