This paper presents an experimentally-proved hydrometallurgical process for selective metals recovery from the waste-printed circuit boards (WPCBs) using a combination of conventional and time-saving methods: leaching, cementation, precipitation, reduction and electrowinning. According to the results obtained in the laboratory tests, 92.4% Cu, 98.5% Pb, 96.8% Ag and over 99% Au could be selectively leached and recovered using mineral acids: sulfuric, nitric and aqua regia. Problematic tin recovery was addressed with comprehensive theoretical and experimental work, so 55.4% of Sn could be recovered through the novel physical method, which consists of two-step phase separation. Based on the results, an integral hydrometallurgical route for selective base and precious metals recovery though consecutive steps, (i) Cu, (ii) Sn, (iii) Pb and Ag, and (iv) Au, was developed. The route was tested at scaled-up laboratory level, confirming feasibility of the process and efficiencies of metals recovery. According to the obtained results, the proposed hydrometallurgical route represents an innovative and promising method for selective metals recovery from WPCBs, particularly applicable in small scale hydrometallurgical environments, focused on medium and high grade WPCBs recycling.

This paper describes the synthesis of tungsten disulfide (WS₂) powder by the sulfurization of tungsten trioxide (WO₃) particles in the presence of additive potassium carbonate (K₂CO₃) in nitrogen (N₂) atmosphere, first at lower temperature (200 °C) and followed by reduction at higher temperature (900 °C). In addition, the ultrasonic spray pyrolysis of ammonium meta-tungstate hydrate (AMT) was used for the production of WO₃ particles at 650 °C in air. The HSC Chemistry^® software package 9.0 was used for the analysis of chemistry and thermodynamic parameters of the processes for WS₂ powder synthesis. The crystalline structure and phase composition of all synthesized powders were analyzed by X-ray diffraction (XRD) measurements. The morphology and chemical composition of these samples were examined by scanning electron microscopy (SEM) combined with energy dispersive X-ray analysis (EDX).

Copper flotation tailings (FTs), resulting from the separation and beneficiation processes of ores, are a significant source of environmental pollution (acid mine drainage, toxic elements leaching, and dust generation). The most common disposal method for this industrial waste is dumping. However, due to their favorable physical and chemical properties—the high content of aluminosilicate minerals (60–90%)—flotation tailings can be effectively treated and reused through geopolymerization technology, thereby adding value to this waste. The objective of this study was to evaluate the potential of utilizing the geopolymerization of FTs to produce sustainable materials. Geopolymers based on natural zeolite (NZ), sodium-modified natural zeolite (NaZ), and fly ash (FA) were prepared using 20%, 35%, and 50% of FTs, activated with a 10 M NaOH solution. The study investigated the influence of Ca/Si, Si/Al, and Na/Al molar ratios on the structural, thermal, and mechanical properties (XRD, TG/DTG and unconfined compressive strength, UCS), and contaminant immobilization (TCLP method) of geopolymers. Geochemical modeling via the PHREEQC program was employed to interpret the results. The findings indicated that the UCS value decreased in zeolite-based geopolymers as the content of FT increased due to the inertness of the tailings and the low calcium content in the system (Ca/Si ≤ 0.3), in contrast to the FA-based geopolymer. The highest UCS of 44.3 MPa was recorded in an FA-based geopolymer containing 50% flotation tailings, with optimal molar ratios of 0.4 for Ca/Si, 3.0 for Si/Al, and 1.1 for Na/Al. In conclusion, the geopolymerization process has been determined to be a suitable technological approach for the sustainable treatment and reuse of FTs.

By-products from zinc hydrometallurgy are classified as hazardous waste with strong leaching toxicities. Even though numerous research papers are dedicated to valorizing valuable metals in it, the primary management route is still disposal or partial reuse, such as the Waelz process. Presented experimental research investigates possibilities of sulfidization and further processing as a technologically sustainable route for valuable metals valorization from non-standard jarosite-PbAg sludge. The comprehensive thermodynamic analysis was done by HSC Chemistry^®, through optimizing process parameters, i.e., temperature, sulfur addition, and selection of possible additives. Technological possibility of magnetic separation, flotation, and smelting of sulfidized material was also investigated; the results were below the values that allow practical application, due to the obtained texture of sulfidized jarosite, which does not allow the liberation of minerals. Smelting tests were performed on sulfidized jarosite with sulfur and without and with carbon as additive. By smelting sulfidized jarosite-PbAg sludge with added carbon in sulfidization stage at 1375 °C, obtained products were matte, slag, raw lead, and dust in which base, critical, and slag forming components were valorized. Valuable metals were concentrated in smelting products so as to enable further processing, which also could be interesting in the case of treatment of complex, polymetallic, and refractory primary materials, which represent a significant contribution to the circular economy.