Acid mine drainage (AMD) is a waste from mining sites, usually acidic, with high concentrations of sulfates and heavy metal ions. This study investigates the AMD neutralization process using fly ash (FA) as an alternative material. Samples of FA from coal-fired power plants in Serbia (“Nikola Tesla” (EF) and “Kostolac” (KOST)) were analyzed and used. The results were compared with the treatment efficiency of commercial neutralization agent (NaOH). The alkaline nature of FA was the basis for use in the treatment process of the extremely acid Lake Robule (pH 2.46), located in the mining areas of eastern Serbia. The optimal S/L ratio for the AMD neutralization process determined for EF was 25 wt.%, and for KOST it was 20 wt.%. The mechanism of the neutralization process was analyzed using the ANC test and PHREEQC program. The element concentrations and pH values in solutions indicated that FA samples could neutralize Lake Robule with more than 99% of Al, Fe, Cu, Zn, and more than 89% of Pb precipitated. Formation of insoluble (oxy)hydroxide forms (Fe³⁺ and Al³⁺ ions) creates favorable conditions for co-precipitation of other trace metals (Cu, Zn, Ni, Pb, and Cd) from AMD, which is further enhanced by cation adsorption on FA particles. FA proved to be a more effective neutralization agent than NaOH due to its adsorption effect, while among the FA samples, KOST was more effective due to the aging process through the carbonization reaction. Using FA as an alternative material is a promising and sustainable method for treating AMD, with economic and environmental benefits.

This paper examines sustainable industrial practices in Serbia, particularly in the mining and energy sector, focusing on the potential of flotation tailings and fly ash, as materials with the largest share in disposed waste in Serbia in 2023 (95%). It highlights the environmental challenges of mining waste and explores innovative approaches to waste management within the circular economy framework. The study analyzes the current state of mining waste in Serbia, particularly in copper mining regions in the east of the country. It discusses the potential for metal recovery from waste and its reuse in various industries. The research also investigates the use of fly ash from thermal power plants as a valuable resource in the construction industry and other sectors. The paper reviews existing initiatives and legislation in Serbia in order to promote sustainable mining practices and waste utilization. By presenting case studies and potential applications, the study demonstrates how implementing circular economy principles in the mining sector can contribute to environmental protection, resource conservation, and economic growth in Serbia. The comprehensive overview of the current state in Serbia provides a solid foundation for establishing a higher degree of circularity in the mining and energy sectors.

Copper flotation tailings (FTs), resulting from the separation and beneficiation processes of ores, are a significant source of environmental pollution (acid mine drainage, toxic elements leaching, and dust generation). The most common disposal method for this industrial waste is dumping. However, due to their favorable physical and chemical properties—the high content of aluminosilicate minerals (60–90%)—flotation tailings can be effectively treated and reused through geopolymerization technology, thereby adding value to this waste. The objective of this study was to evaluate the potential of utilizing the geopolymerization of FTs to produce sustainable materials. Geopolymers based on natural zeolite (NZ), sodium-modified natural zeolite (NaZ), and fly ash (FA) were prepared using 20%, 35%, and 50% of FTs, activated with a 10 M NaOH solution. The study investigated the influence of Ca/Si, Si/Al, and Na/Al molar ratios on the structural, thermal, and mechanical properties (XRD, TG/DTG and unconfined compressive strength, UCS), and contaminant immobilization (TCLP method) of geopolymers. Geochemical modeling via the PHREEQC program was employed to interpret the results. The findings indicated that the UCS value decreased in zeolite-based geopolymers as the content of FT increased due to the inertness of the tailings and the low calcium content in the system (Ca/Si ≤ 0.3), in contrast to the FA-based geopolymer. The highest UCS of 44.3 MPa was recorded in an FA-based geopolymer containing 50% flotation tailings, with optimal molar ratios of 0.4 for Ca/Si, 3.0 for Si/Al, and 1.1 for Na/Al. In conclusion, the geopolymerization process has been determined to be a suitable technological approach for the sustainable treatment and reuse of FTs.

Reuse of waste is one of the main principles of sustainable development and circular economy. Secondary alkaline lead slag is a hazardous waste generated in the recycling process of lead-acid batteries that may be suitable in construction materials. The environmental impact of the use of lead slag as a partial replacement of fine aggregates in the cement-based stabilization/solidification (S/S) process for the preparation of concrete was studied in this paper. Solidified products containing 10%, 15%, 20%, and 25% slag were laboratory tested by unconfined compressive strength (UCS) analyses and the Toxicity Characteristic Leaching Procedure (TCLP). At the same time, the leachability of toxic elements from solidified products with a high percent of slag was evaluated under environmental conditions for during one year. The results of the UCS and TCLP indicated that utilization of this type of slag in cement-based applications may be justified with its controlled addition. However, the described application of the slag was disputed due to the high release of As under high alkaline environmental conditions. Eh-pH analyses and the geochemical modeling using the software PHREEQC were evaluated, as well as the mechanism of pollutant (Pb, As) immobilization (precipitation, adsorption) as a function of pH conditions.

Natural zeolites (NatZ) are widely available, porous, crystalline aluminosilicate minerals that are commonly used as cost-effective adsorbents in water treatment processes. Despite their efficiency in removing various heavy metal ions from wastewater, NatZ show relatively low affinity toward Ni²⁺ and Cr³⁺ ions. This study aimed to develop composite adsorbents based on NatZ and hydroxyapatite using two methods, hydrothermal and mechanochemical, and their adsorption properties for the removal of Ni²⁺ and Cr³⁺ ions from aqueous solutions were investigated. X-ray powder diffraction and scanning electron microscopy analyses confirmed that under hydrothermal conditions, needle-like hydroxyapatite crystals were formed on the surface of NatZ, while the zeolite structure remained unchanged. Compared to the mechanochemically prepared sample, this adsorbent showed higher efficiency, binding 6.91 mg Ni²⁺/g and 16.95 mg Cr³⁺/g. Adsorption kinetics of the tested cations in both cases can be described by a pseudo-second-order model (R² is higher than 0.95 for all adsorbents). It is concluded that the presence of hydroxyapatite on the zeolite surface significantly improves the adsorption performance of NatZ, demonstrating its potential for the removal of heavy metal ions in wastewater treatment.