Background and Objectives: This study aimed to evaluate the surface roughness evolution of several finished and polished composites when bleaching materials are applied. The research was conducted on four microhybrid or nanofilled composites that are used in dental restorations. Materials and Methods: For each composite type, 5 samples were selected for control, 5 samples were subjected to the bleaching protocol “office bleach” with 40% hydrogen peroxide, and 5 other samples were subjected to the “home bleach” protocol with 16% carbamide peroxide, resulting in a total number of 60 samples. The surfaces of all the samples were tested for roughness, and the values of the most relevant parameter (Ra), were collected. Comparisons between composites and samples were performed using one-way ANOVA (in Statistical Package for Social Sciences). Results: After the bleaching protocol with 40% hydrogen peroxide gel, it was found that the roughness of the group increased considerably compared to the control group, so the highest roughness was found at GC Gradia direct anterior group, and the lowest value was registered for the 3M ESPE Valux Plus group. Following the bleaching protocol with 16% carbamide peroxide (home bleach), it was noted that the sample surfaces were not as affected. In this case, the lowest roughness was found at 3M ESPE Valux Plus group, and the highest roughness was registered for the GC G-aenial anterior group. Following the interpretation of the results, all four types of dental composites tested showed significant surface roughness differences between the groups subjected to bleaching protocols and those kept as control (p < 0.05). Conclusions: The surfaces of the samples were affected by the bleaching protocols by increasing the roughness compared to the control samples.

Ti-based alloys are an important class of materials suitable especially for medical applications, but they are also used in the industrial sector. Due to their low tribological properties it is necessary to find optimal technologies and alloying elements in order to develop new alloys with improved properties. In this paper, a study on the influence of sintering treatments on the final properties of a titanium alloy is presented. The alloy of interest was obtained using the powders in following weight ratio: 80% wt Ti, 8% wt Mn, 3% wt Sn, 6% wt Aluminix123, 2% wt Zr and 1% wt graphite. Two sintering methods were used, namely two-step sintering (TSS) and multiple-step sintering (MSS), as alternatives to conventional sintering which uses a single sintering dwell time. Evolution of sample morphology, composition and crystalline structure with sintering method was evidenced. The lower values for the friction coefficient and for the wear rate was attained in the case of the sample obtained by TSS.

The current strategy for treating osteomyelitis includes surgical procedures for complete debridement of the formed biofilm and necrotic tissues, systemic and oral antibiotic therapy, and the clinical use of cements and three-dimensional scaffolds as bone defect fillers and delivery systems for therapeutic agents. The aim of our research was to formulate a low-cost hybrid nanoparticulate biomaterial using poly(lactic-co-glycolic acid) (PLGA), in which we incorporated the therapeutic agent (ciprofloxacin), and to deposit this material on titanium plates using the matrix-assisted pulsed laser evaporation (MAPLE) technique. The deposited material demonstrated antibacterial properties, with all analyzed samples inhibiting the growth of tested bacterial strains, confirming the release of active substances from the investigated biocomposite. The poly(lactic-co-glycolic acid)-ciprofloxacin (PLGA-CIP) nanoparticle scaffolds displayed a prolonged local sustained release profile over a period of 45 days, which shows great promise in bone infections. Furthermore, the burst release ensures a highly efficient concentration, followed by a constant sustained release which allows the drug to remain in the implant-adjacent area for an extended time period.

Nowadays, the state-of-the-art discoveries in the field of delivery systems for therapeutic purposes have redefined the importance of biocompatible and biodegradable poly(lactic-co-glycolic acid (PLGA) nanocomposites. The study aimed to obtain a biocomposite material, with improved properties of its constituents [zinc-boron (Zn-B) complex and PLGA], by a simple, cost-effective method. The water/oil/water double emulsion technique allowed the adjustment of the synthesis parameters, to maximize the degree of Zn-B complex encapsulation. The morphological aspects of the samples were established by scanning electron microscopy (SEM). Particle size distribution was determined by dynamic light scattering (DLS). Morphology was typical for PLGA, spherical one. Depending on the synthesis conditions, the obtained particles have diameters between 10-450 nm. Zeta potential (ZP) showed that the particles have electronegative surface charge, offering a favorable perspective on aggregation, flocculation, and dispersion phenomena. It was observed, applying the design of experiments, that the particles size increased with increasing amounts of PLGA and polyvinyl alcohol (PVA), while ZP increased with higher PLGA and smaller PVA amounts in the formulation. The encapsulation efficiency was determined by ultra-high performance liquid chromatography/mass spectrometry (UHPLC/MS). The in vitro assessment was performed using Vero CCL-81 epithelial cell line and the 3-(4,5-Dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) test. Zn-B-PLGA biocomposite has promising characteristics and can be used for future biomedical applications.

The paper presents the results of experimental researches on the formation of barium hexaferrite type M (BHFM) by microwave heating. The microwave heating process takes only a few minutes to obtain calcined barium ferrite powders. Micronic and nanometric powders of BaCO3 and α-Fe2O3 were used as raw materials. In order to obtain BHFM, the microwave heating process was used with following mixtures: stoichiometric homogeneous mixture of BaCO3 and α-Fe2O3 powders, mechanically alloyed mixtures of BaCO3 and α-Fe2O3 powders for 5 and 20 hours in wet medium using a high energy ball mill Pulverisette 4. Using high energy ball milling, the powder size was turned into nanoscale. After using the microwave heating process it was observed a significant reduction of temperature-time parameters to BHFM formation for mechanically alloyed mixtures compared to homogeneous mixture.