In this work, the causes of porosity of TiAlN hard coatings sputter deposited on D2 tool steel were studied since its corrosion resistance is mainly affected by imperfections within the coating (e.g., pinholes, pores, crevices). The corrosion test was performed in a chlorine solution using electrochemical impedance spectroscopy. The coating morphology of growth defects before and after the exposure was studied by scanning electron microscopy (SEM), while focused ion beam (FIB) was used to make series of cross-sections through individual selected defects. We confirm that pitting corrosion is closely related to the through-thickness growth defects. It was also found that in the case of nodular defects, the intensity of corrosion depends on the shape of the seed.

In this work, we investigated a novel Al-Mg-Si alloy, which was developed from an AA 6082, in order to considerably improve the yield and tensile strengths whilst retain excellent ductility. The new alloy possesses a higher content of Si than specified by AA 6082, and, in addition, it contains copper and zirconium. The alloy was characterized in the as-cast condition, after homogenization, extrusion, and T6 heat treatment using light microscopy, scanning and transmission electron microscopy with energy dispersive spectrometry, X-ray diffraction, differential thermal analysis and tensile testing. After T6 temper, tensile strengths were around 490 MPa with more than 10% elongation at fracture. The microstructure consisted of small-grained Al-rich matrix with α-AlMnSi and Al₃Zr dispersoids, and Q′-AlCuMgSi and β-Mg₂Si-type precipitates.

A comprehensive experimental investigation of the wear behaviour of coated spur polymer gears made of POM is performed in this study. The three physical vapour deposition (PVD) coatings investigated were aluminium (Al), chromium (Cr), and chromium nitrite (CrN). Al was deposited in three process steps: By plasma activation, metallisation of Al by the magnetron sputtering process, and by plasma polymerisation. Cr deposition was performed in only one step, namely, the metallization of Cr by the magnetron sputtering process. The deposition of CrN was carried out in two steps: the first involved the metallization of Cr by the magnetron sputtering process while the second step, vapour deposition, involved the reactive metallisation of Cr with nitrogen, also by the magnetron sputtering process. The gears were tested on an in-house developed testing rig for different torques (16, 20, 24 and 30 Nm) and rotational speed of 1000 rpm. The duration of the experiments was set to 13 h, when the tooth thickness, and, consequently, the wear of the tooth flank was recorded. The experimental results showed that the influence of metallisation with aluminium, chromium, and chromium nitrite surface coatings on the wear behaviour of the analysed polymer gear is not significant. This is probably due to the fact that the analysed coatings were, in all cases, very thin (less than 500 nm), and therefore did not influence the wear resistance significantly. In that respect, an additional testing using thicker coatings should be applied in the further research work.

The aluminium alloy AA 6086 attains the highest room temperature strength among Al-Mg-Si alloys. This work studies the effect of Sc and Y on the formation of dispersoids in this alloy, especially L1₂-type ones, which can increase its high-temperature strength. A comprehensive investigation was carried out using light microscopy (LM), scanning (SEM), and transmission (TEM) electron microscopy, energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), differential scanning calorimetry (DSC), and dilatometry to obtain the information regarding the mechanisms and kinetics of dispersoid formation, particularly during isothermal treatments. Sc and Y caused the formation of L1₂ dispersoids during heating to homogenization temperature and homogenization of the alloys, and during isothermal heat treatments of the as-cast alloys (T5 temper). The highest hardness of Sc and (Sc + Y) modified alloys was attained by heat-treating alloys in the as-cast state in the temperature range between 350 °C and 450 °C (via T5 temper).

In this work, the ageing of some Al-Mn-Cu-Be alloys was investigated in the temperature range in which predominantly icosahedral quasicrystalline (IQC) precipitates can form. The alloys were cast into a copper mould, directly aged (T5 heat treatment) between 300 and 440 °C for different times. Afterwards, they were examined using scanning and transmission electron microscopy, X-ray diffraction and hardness testing. The main aim of the work was to determine the conditions at which a high number density of spherical icosahedral quasicrystalline precipitates can form. The highest number density of IQC precipitates was obtained at 300 °C after prolonged ageing. The spheroidal precipitates had a diameter less than 20 nm. The size of IQC precipitates increased with the increasing temperature, and in addition, decagonal quasicrystalline precipitates appeared. The time to maximum hardness decreased strongly with increasing ageing temperature. The IQC precipitates can form in a fairly broad temperature range in Al-Mn-Cu-Be alloys and that by varying ageing temperature and duration, rather different distributions of precipitates can be obtained. The presence of precipitates caused rather strong aluminium alloys and fast work hardening during initial plastic deformation.