A357 samples were realized by laser powder bed fusion (LPBF) on building platforms heated up to different temperatures. The effect of the preheating temperature and of the post processing heat treatment on the microstructure and the mechanical properties of the samples was studied. It was demonstrated that building platform heating can act as an in situ ageing heat treatment following the fast cooling that arises during laser scanning. A 17% higher ultimate tensile strength was achieved by the selection of the optimum building platform temperature. Moreover, the possibility to further increase the mechanical properties by means of a direct ageing heat treatment was investigated.

Two-dimensional graphene nanoplatelets with unique electrical, mechanical and thermophysical characteristics are considered as an interesting reinforcement to develop new lightweight, high-strength, and high-performance metal matrix nanocomposites. On the other hand, by the rapid progress of technology in recent years, development of advanced materials like new metal matrix nanocomposites for structural engineering and functional device applications is a priority for various industries. This article provides an overview of research efforts with an emphasis on the fabrication and characterization of different metal matrix nanocomposites reinforced by graphene nanoplatelets (GNPs). Particular attention is devoted to find the role of GNPs on the final electrical and thermal conductivity, the coefficient of thermal expansion, and mechanical responses of aluminum, magnesium and copper matrix nanocomposites. In sum, this review pays specific attention to the structure-property relationship of these novel nanocomposites.

This article provides an overview of research efforts with an emphasis on the fabrication of metal matrix nanocomposites (MMNCs) reinforced by graphene nanoplatelets (GNPs). Particular attention is devoted to finding the challenges in the production of MMNCs through the powder metallurgy techniques. The main technical challenges can be listed as: (I) reinforcement selection; (II) dispersion of reinforcement within the matrix; (III) reactivity between the reinforcement and matrix; (IV) interfacial bonding; (V) preferred orientation of reinforcement. It is found that some of these difficulties can be attributed to the nature of the materials involved, while the others are related to the preparation routes. It is reported that the challenges related to the process can often be addressed by changing the production process or by using post-processing techniques. More challenging issues instead are related to the composition of the matrix and reinforcement, their reactivity and the dispersion of reinforcement. These topics still bring significant challenges to the materials scientists, and it would be worth mentioning that the fabrication of MMNCs with a uniform dispersion of reinforcement, strong interfacial bonding, without detrimental reactions and improved isotropic properties is still a puzzling issue.

Al-Si-Zn-Mg-Cu samples were produced using Laser Powder Bed Fusion from mixed AlSi10Mg and 7075 powders. It was observed that the introduction of silicon to an Al-Zn-Mg-Cu alloy strongly reduced the crack density, probably because of the reduction of the solidification range, the improved fluidity of the molten phase and the reduction of the coefficient of thermal expansion. The density measurements showed that crack-free samples can be successfully produced with this powder mixture. The obtained Al-Si-Zn-Mg-Cu samples were characterized in terms of microstructure, hardness and tensile properties showing that this composition is very promising for future powder bed additive manufacturing processes.