Metals that come into contact with the body can cause reactions in the body, so biomaterials must be tested to avoid side effects. Mo, Zr, and Ta are non-toxic elements; alloyed with titanium, they have very good biocompatibility properties and mechanical properties. The paper aims to study an original Ti20Mo7ZrxTa system (5, 10, 15 wt %) from a mechanical and in vitro biocompatibility point of view. Alloys were examined by optical microstructure, tensile strength, fractographic analysis, and in vitro assay. The obtained results indicate very good mechanical and biological properties, recommending them for future orthopedic medical applications.

The subject of Mg-based biodegradable materials, used for medical applications, has been extensively studied throughout the years. It is a known fact that alloying Mg with biocompatible and non-toxic elements improves the biodegradability of the alloys that are being used in the field of surgical applications. The aim of this research is to investigate the aspects concerning the microstructure, electrochemical response (corrosion resistance) and in vitro cytocompatibility of a new experimental Mg-based biodegradable alloy—Mg–0.5%Ca with controlled addition of Gd as follows: 0.5, 1.0, 1.5, 2.0 and 3.0 wt.%—in order to establish improved biocompatibility with the human hard and soft tissues at a stable biodegradable rate. For this purpose, scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), light microscopy (LM) and X-ray diffraction (XRD) were used for determining the microstructure and chemical composition of the studied alloy and the linear polarization resistance (LPR) method was used to calculate the corrosion rate for the biodegradability rate assessment. The cellular response was evaluated using the 3-(4,5-dimethyltiazol-2-yl)-2,5-diphenyl tetrazolium bromide (MTT) test followed by fluorescence microscopy observation. The research led to the discovery of a dendritic α-Mg solid solution, as well as a lamellar Mg₂Ca and a Mg₅Gd intermetallic compound. The in vivo tests revealed 73–80% viability of the cells registered at 3 days and between 77 and 100% for 5 days, a fact that leads us to believe that the experimental studied alloys do not have a cytotoxic character and are suitable for medical applications.

In recent years, biodegradable Mg-based materials have been increasingly studied to be used in the medical industry and beyond. A way to improve biodegradability rate in sync with the healing process of the natural human bone is to alloy Mg with other biocompatible elements. The aim of this research was to improve biodegradability rate and biocompatibility of Mg-0.5Ca alloy through addition of Y in 0.5/1.0/1.5/2.0/3.0wt.%. To characterize the chemical composition and microstructure of experimental Mg alloys, scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), light microscopy (LM), and X-ray diffraction (XRD) were used. The linear polarization resistance (LPR) method was used to calculate corrosion rate as a measure of biodegradability rate. The cytocompatibility was evaluated by MTT assay (3-(4,5-dimethylthiazole-2-yl)-2,5-diphenyltetrazolium bromide) and fluorescence microscopy. Depending on chemical composition, the dendritic α-Mg solid solution, as well as lamellar Mg₂Ca and Mg₂₄Y₅ intermetallic compounds were found. The lower biodegradability rates were found for Mg-0.5Ca-2.0Y and Mg-0.5Ca-3.0Y which have correlated with values of cell viability. The addition of 2–3 wt.%Y in the Mg-0.5Ca alloy improved both the biodegradability rate and cytocompatibility behavior.

Mihaela Andreea Mitiu, Maria Iuliana Marcus, Maria Vlad, Cristina Mihaela Balaceanu - Stability of Ceramic Glazes Obtained by Valorification of Anorganic Pigments Extracted from Electroplating Sludge

Mg-based biodegradable materials, used for medical applications, have been extensively studied in the past decades. The in vitro cytocompatibility study showed that the proliferation and viability (as assessed by quantitative MTT-assay—3-(4,5-dimethyltiazol-2-yl)-2,5-diphenyl tetrazolium bromide) were not negatively affected with time by the addition of Mn as an alloying element. In this sense, it should be put forward that the studied alloys don’t have a cytotoxic effect according to the standard ISO 10993-5, i.e., the level of the cells’ viability (cultured with the studied experimental alloys) attained both after 1 day and 5 days was over 82% (i.e., 82, 43–89, 65%). Furthermore, the fibroblastic cells showed variable morphology (evidenced by fluorescence microscopy) related to the alloy sample’s proximity (i.e., related to the variation on the Ca, Mg, and Mn ionic concentration as a result of alloy degradation). It should be mentioned that the cells presented a polygonal morphology with large cytoplasmic processes in the vicinity of the alloy’s samples, and a bipolar morphology in the remote region of the wells. Moreover, the in vitro results seem to indicate that only 0.5% Mn is sufficient to improve the chemical stability, and thus the cytocompatibility; from this point of view, it could provide some flexibility in choosing the right alloy for a specific medical application, depending on the specific parameters of each alloy, such as its mechanical properties and corrosion resistance. In order to assess the in vivo compatibility of each concentration of alloy, the pieces were implanted in four rats, in two distinct body regions, i.e., the lumbar and thigh. The body’s reaction was followed over time, 60 days, both by general clinical examinations considering macroscopic changes, and by laboratory examinations, which revealed macroscopic and microscopic changes using X-rays, CT(Computed Tomography), histology exams and SEM (Scanning Electron Microscopy). In both anatomical regions, for each of the tested alloys, deformations were observed, i.e., a local reaction of different intensities, starting the day after surgery. The release of hydrogen gas that forms during Mg alloy degradation occurred immediately after implantation in all five of the groups examined, which did not affect the normal functionality of the tissues surrounding the implants. Imaging examinations (radiological and CT) revealed the presence of the alloy and the volume of hydrogen gas in the lumbar and femoral region in varying amounts. The biodegradable alloys in the Mg-Ca-Mn system have great potential to be used in orthopedic applications.