This study assessed the influence of rapid 3 s light curing on the new generation of bulk-fill resin composites under the simulated aging challenge and depths up to 4 mm. Four bulk-fill materials were tested: two materials designed for rapid curing (Tetric PowerFill—PFILL; Tetric PowerFlow—PFLW) and two regular materials (Filtek One Bulk Fill Restorative—FIL; SDR Plus Bulk Fill Flowable—SDR). Three-point bending (n = 10) was used to measure flexural strength (FS) and flexural modulus (FM). In the 3 s group, two 2 mm thick specimens were stacked to obtain 4 mm thickness, while 2 mm-thick specimens were used for ISO group. Specimens were aged for 1, 30, or 30 + 3 days in ethanol. The degree of conversion (DC) up to 4 mm was measured by Raman spectroscopy. There was no difference between curing protocols in FS after 1 day for all materials except PFLW. FM was higher for all materials for ISO curing protocol. Mechanical properties deteriorated by increasing depth (2–4 mm) and aging. ISO curing induced higher DC for PFLW and FIL, while 3 s curing was sufficient for PFILL and SDR. The 3 s curing negatively affected FM of all tested materials, whereas its influence on FS and DC was highly material-specific.

The objective of this study was to compare the polymerization kinetics of bulk-fill resin composites cured with a LED-curing device and a diode laser (449 nm). Three bulk-fill composites were light-cured with constant radiation exposure at 10 J/cm² by varying radiant exitance and curing time. The following three light-curing protocols were used: (I) 3300 mW/cm² for 3 s; (II) 2000 mW/cm² for 5 s; and (III) 1000 mW/cm² for 10 s. The degree of conversion (DC) was monitored in real time at a data acquisition rate of 2 spectra/s over a 5-min period and again after seven days using Fourier transform infrared spectroscopy. DC amounted to 30.9–61.7% at 4-mm depth after 5 min. DC values of two sculptable composites were significantly higher with the laser, regardless of the curing protocol used, but not for the flowable composite. The maximum polymerization rate (2.0–22.1%/s) was less affected by the type of curing device for one of the composites, while the other two composites achieved significantly higher values when cured with the laser. Laser curing generally increased the DC and the maximum polymerization rate while it shortened the onset of the maximum reaction rate. New handheld laser devices with adjustable power have the potential to be used as a photopolymerization light source for new generations of bulk-fill composites.

The aim of this work was to determine if PAW (Plasma Activated Water) seed treatment and growing conditions could have positive effects on lettuce seedlings and growth. The paper presents the results of a pot experiment on lettuce (Lactuca sativa L.) cultivation in greenhouse and field conditions after seed treatment with PAW. The experiment was conducted in two consecutive seasons in 2021 and 2022 and the following growth parameters were measured: head mass, rosette height, rosette width, number of leaves, root mass and root length. As a result of the study, it was found that lettuces grown in the greenhouse from PAW treated seeds had higher results in the first measurement for both cultivars (mass 32.26%, diameter 19.01%, number of leaves 13.49% and height 24.01%), while there were no statistically significant effects on the root system. The lowest results were obtained in untreated and field-grown plants. In addition, plant dry matter was measured and it was found that plants grown from PAW treated seeds had a higher percentage of dry matter (11.51% in 2021, and 11.58% in 2022). It was also found that cultivation in greenhouse resulted in a better quality of plants than the cultivation in the open field.

We present mcRS, a high-sensitivity free-space optics Raman system for in situ mechanochemical monitoring. It improves spectral and time resolution, costs five times less than commercial systems, and uniquely enables simultaneous rheology monitoring.

In this study, the morphological, pomological, and nutritional values of wild and cultivated rosehip fruits grown in the Slavonia region of eastern Croatia were studied. The results revealed significant differences in several morphological and pomological characteristics among the rosehip genotypes in terms of fruit weight, flesh weight, seed weight, and fruit flesh ratio, with no significant differences in fruit width, fruit length, fruit shape index, seed number per fruit, or seed length. The evaluated rosehip fruit genotypes differed significantly from each other in terms of hectoliter weight (kg), fruit bulk (cm3), and bulk density (kg/m3). For water–soluble extracts, ash, and pH, no statistical difference was found between naturally grown genotypes, but there was a significant difference between naturally grown and cultivated genotypes. Twenty-three major and trace elements were analyzed. The most abundant elements were K, Ca, Mg, and P in both cultivated and naturally grown fruits. The highest concentrations of microelements were Fe, Al, Mn, and Sr. The conventionally cultivated genotype L1 had the highest concentration of Fe and Na as essential elements for humans but also had the highest concentrations of Al, Sr, Ti, V, Cr, Pb, Co, Li, and As of all the genotypes studied. The naturally grown genotype L4 had the highest concentrations of S, Zn, Rb, and Cd and the lowest concentrations of Mg, K, and Ca among all studied genotypes. The data showed that the analyzed genotypes from eastern Croatia had good nutritional quality and variability, making them suitable as genetic resources and possibly leading to the detection of rosehip genotypes as potential sources of beneficial ingredients for human health.