Duplex stainless steel powders for laser additive manufacturing have not been developed extensively. In this study, the melts of a super duplex stainless steel X2CrNiMoCuWN25-7-4 (AISI F55, 1.4501) were atomized with different process gases (Ar or N₂) at different atomization gas temperatures. The process gas N₂ in the melting chamber leads to a higher nitrogen dissolution in the steel and a higher nitrogen content of the atomized powders. The argon-atomized powders have more gas porosity inside the particles than the nitrogen-atomized powders. In addition, the higher the atomization gas temperature, the finer the powder particles. The duplex stainless steel powders showed good processability during PBF-LB/M (Laser powder bed fusion). The gas entrapment in the powder particles, regardless of the gas chemistry and the gas content, appears to have a negligible effect on the porosity of the as-built parts.

Laser additively manufactured duplex stainless steels contain mostly ferrite in the as-built parts due to rapid solidification of the printed layers. To achieve duplex microstructures (ferrite and austenite in roughly equal proportions) and, thus, a good combination of mechanical properties and corrosion resistance, an austenitic stainless steel powder (X2CrNiMo17-12-2) and a super duplex stainless steel powder (X2CrNiMoN25-7-4) were mixed in different proportions and the powder mixtures were processed via PBF-LB/M (Laser Powder Bed Fusion) under various processing conditions by varying the laser power and the laser scanning speed. The optimal process parameters for dense as-built parts were determined by means of light optical microscopy and density measurements. The austenitic and ferritic phase formation of the mixed alloys was significantly influenced by the chemical composition adjusted by powder mixing and the laser energy input during PBF-LB/M. The austenite content increases, on the one hand, with an increasing proportion of X2CrNiMo17-12-2 in the powder mixtures and on the other hand with increasing laser energy input. The latter phenomenon could be attributed to a slower solidification and a higher melt pool homogeneity with increasing energy input influencing the phase formation during solidification and cooling. The desired duplex microstructures could be achieved by mixing the X2CrNiMo17-12-2 powder and the X2CrNiMoN25-7-4 powder at a specific mixing ratio and building with the optimal PBF-LB/M parameters.

Nitriding can significantly increase the load carrying properties of gears. While the diffusion layer is primarily responsible for improving the tooth root and flank load carrying capacity, the compound layer mainly determines the tribological properties of the gear surface. In the present work, the influence of the compound layer on the tribological load carrying capacity of nitrided gears in the N/N pairing was investigated. For this purpose, compound layers with different thickness, porosity and phase composition were produced and their micro-pitting and wear behavior were investigated in load stage and speed stage tests. The test results confirm that the properties of the compound layer are decisive for the micro-pitting and wear resistance of nitrided gears. For a high micro-pitting resistance, the presence of pores in the near-surface area of the compound layer is of high importance, since no micro-pitting occurred as long as pores were present. With regard to the wear behavior, no dependence on the compound layer thickness or the porous zone thickness was found while the phase composition of the compound layer shows a decisive influence.