A typical ballistic protection helmet for ground military troops has an inside laminate polymer composite reinforced with 19 layers of the aramid, which are neither recyclable or biodegradable and are relatively expensive. The hybridization of synthetic aramid with a natural lignocellulosic fiber (NLF) can provide a lower cost and desirable sustainability to the helmet. In the present work, the curaua fiber, one of the strongest NLFs, is, for the first time, considered in non-woven mat layers to partially replace the aramid woven fabric layers. To investigate the possible advantage of this replacement, the tensile and impact properties of aramid/curaua hybrid laminated composites intended for ballistic helmets, in which up to four layers of curaua were substituted for the aramid, were evaluated. Tensile strength, toughness, and elastic modulus decreased with the replacement of the aramid while the deformation of rupture was improved for the replacement of nine aramid layers by two layers of curaua. Preliminary impact tests corroborate the decreasing tendency found in the tensile properties with the replacement of the aramid by curaua. Novel proposed Reduction Maps showed that, except for the replacement of four aramid layers by one layer of curaua, the decrease percentage of any tensile property value was lower than the corresponding volume percentage of replaced aramid, which revealed advantageous hybridization for the replacement of nine or more aramid layers.

Curaua, as a leaf-based natural fiber, appears to be a promising component with aramid fabric reinforcement of hybrid composites. This work deals with the investigation of flexural, impact and elastic properties of non-woven curaua–aramid fabric hybrid epoxy composites. Five configurations of hybrid composites in a curaua non-woven mat with an increasing quantity of layers, up to four layers, were laminated through the conventional hand lay-up method. The proposed configurations were idealized with at least 60 wt% reinforcement in the non-alternating configuration. As a result, it was observed that the flexural strength decreased by 33% and the flexural modulus by 56%. In addition, the energy absorbed in the Charpy impact also decreased in the same proportion as the replaced amount of aramid. Through the impulse excitation technique, it was possible observe that the replacement of the aramid layers with the curaua layers resulted in decreased elastic properties. However, reduction maps revealed proportional advantages in hybridizing the curaua with the aramid fiber. Moreover, the hybrid composite produced an almost continuous and homogeneous material, reducing the possibility of delamination and transverse deformation, which revealed an impact-resistant performance.

Hybrid composites are expanding applications in cutting-edge technology industries, which need materials capable of meeting combined properties in order to guarantee high performance and cost-effectiveness. This original article aimed for the first time to investigate the hybrid laminated composite thermal behavior, made of two types of fibers: synthetic Twaron^® fabric and natural curaua non-woven mat, reinforcing epoxy matrix. The composite processing was based on the ballistic helmets methodology from the North American Personal Armor System for Ground Troops, currently used by the Brazilian Army, aiming at reduced costs, total weight, and environmental impact associated with the material without compromising ballistic performance. Thermal properties of plain epoxy, aramid fabric, and curaua mat were evaluated, as well as the other five configurations of hybrid laminated composites. These properties were compared using thermogravimetric analysis (TGA) with its derivative (DTG), differential thermal analysis (DTA), and thermomechanical analysis (TMA). The results showed that the plain epoxy begins thermal degradation at 208 °C while the curaua mat at 231 °C and the aramid fabric at 477 °C. The hybrid laminated composites curves showed two or three inflections in terms of mass loss. The only sample that underwent thermal expansion was the five-aramid and three-curaua layers composite. In the third analyzed temperature interval, related to the glass transition temperature of the composites, there was, in general, an increasing thermal stability behavior.

The main modifications of thermal and colorimetric parameters after thermal aging of DGEBA/TETA system (plain epoxy) and fique-fiber woven fabric-reinforced epoxy composites are described. As a preliminary study, thermal analysis was carried out on epoxy matrix composites reinforced with 15, 30, 40 and 50% fique-fiber woven fabric. After this previous analysis, the 40% composite was chosen to be thermally aged, at 170 °C. Three exposure times were considered, namely, 0, 72, 120 and 240 h. Samples were studied by thermogravimetric analysis (TGA), differential thermal analysis (DTA), differential scanning calorimetry (DSC), thermomechanical analysis (TMA) and colorimetry analysis. Significant color changes were observed after thermal aging combined with oxidation. It was also found that the thermal behavior of the plain epoxy showed greater resistance after thermal exposure. By contrast, the composites were more sensitive to temperature variations as a result of thermal stresses induced between fique fibers and the epoxy matrix.