Titica vine (Heteropsis flexuosa) is a typical plant of the Amazon region commonly used for making baskets, bags, brooms and furniture, owing to its stiff fibers. In spite of its interesting properties, there is so far no reported information regarding the use of titica vine fibers (TVFs) in engineering composite materials. In this work, the TVF and its epoxy composites were for the first time physically, thermally and mechanically characterized. Additionally, the effect of two kinds of chemical treatments, one with sodium carbonate and one with calcium lignosulfonate, as well as different volume fractions, 10, 20, 30 and 40 vol%, of TVF-reinforced composites were assessed for corresponding basic properties. The thermogravimetric results of the composites reveal enhanced thermal stability for higher TVF content. In addition, the composite incorporated with 40 vol% of TVFs treated with sodium carbonate absorbed 19% more water than the composites with untreated fibers. By contrast, the calcium lignosulfonate treatment decreased water absorption by 8%. The Charpy and Izod impact tests showed that the composites, incorporated with the highest investigated volume fraction (40 vol%) of TVF, significantly increased the absorbed energy by 18% and 28%, respectively, compared to neat epoxy. ANOVA and Tukey statistical analyses displayed no direct influence of the chemical treatments on the energy absorption of the composites for either impact tests. SEM images revealed the main fracture mechanisms responsible for the performance of TVF composites.

Fiber-reinforced composites are among the most investigated and industrially applied materials. Many studies on these composites using fibers, especially with natural fibers, were made in response to an urgent action for ambient preservation. A particularly relevant situation exists nowadays in the area of materials durability. In this respect, no studies on water-immersion-accelerated aging in fique fiber–epoxy composites are reported. This work aimed to fill this gap by investigating the epoxy matrix composites reinforced with 40 vol% fique fabric. The epoxy matrix and the composite, both unaged and aged, were characterized by weight variation, water absorption, morphology, colorimetry (CIELAB method), Fourier transform infrared spectroscopy (FTIR) and dynamic–mechanical analysis (DMA). The main results were that degradation by water presents appearance of complex microfibril structures, plasticization of epoxy resin, and debonding of the fique fiber/epoxy matrix. The most intense color change was obtained for the water-immersion-aged epoxy by 1440 h. Cole–Cole diagrams revealed the heterogeneity of the materials studied.

The titica vine fiber (TVF) (Heteropsis flexuosa) is a natural lignocellulose fiber (NLF) from the Amazon rainforest that was, for the first time, investigated in terms of its basic properties such as dimensions, porosity, and density as well as its chemical composition, moisture content, crystallinity, and microfibrillar angle. In this study, the apparent density of TVF was determined as one of the lowest-ever reported for NLFs). Using both the geometric method and Archimedes’ principle, density values in the range of 0.5–0.6 g/cm³ were obtained. The moisture content was measured as around 11%, which is in accordance with the commonly reported values for NLFs. The TVF exhibited a high porosity, approximately 70%, which was confirmed by SEM images, where a highly porous morphological structure associated with the presence of many voids and lumens was observed. The crystallinity index and microfibrillar angle were determined as 78% and 7.95°, respectively, which are of interest for a stiff NLF. A preliminary assessment on the mechanical properties of the TVFs revealed a tensile strength, Young’s modulus, and elongation of 26 MPa, 1 GPa, and 7.4%, respectively. Furthermore, the fiber presented a critical length of 7.62 mm in epoxy matrix and an interfacial shear strength of 0.97 MPa. These results suggest the TVFs might favors applications where lighter materials with intermediate properties are required.

Seeking to improve personal armor equipment by providing mobility and resistance to penetration, this research aimed to explore the potential of sustainable materials in order to assess their ability in ballistic applications. Titica vine fibers (TVFs) extracted from aerial roots of Heteropsis flexuosa from the Amazon region were incorporated at 10, 20, 30, and 40 vol% into an epoxy matrix for applications in ballistic multilayered armor systems (MASs) and stand-alone tests for personal protection against high-velocity 7.62 mm ammunition. The back-face signature (BFS) depth measured for composites with 20 and 40 vol% TVFs used as an intermediate layer in MASs was 25.6 and 32.5 mm, respectively, and below the maximum limit of 44 mm set by the international standard. Fracture mechanisms found by scanning electron microscopy (SEM) attested the relevance of increasing the fiber content for applications in MASs. The results of stand-alone tests showed that the control (0 vol%) and samples with 20 vol% TVFs absorbed the highest impact energy (E_abs) (212–176 J), and consequently displayed limit velocity (V_L) values (213–194 m/s), when compared with 40 vol% fiber composites. However, the macroscopic evaluation found that, referring to the control samples, the plain epoxy shattered completely. In addition, for 10 and 20 vol% TVFs, the composites were fragmented or exhibited delamination fractures, which compromised their physical integrity. On the other hand, composites with 30 and 40 vol% TVFs, whose E_abs and V_L varied between 166–130 J and 189–167 m/s, respectively, showed the best physical stability. The SEM images indicated that for composites with 10 and 20 vol% TVFs, the fracture mode was predominantly brittle due to the greater participation of the epoxy resin and the discrete action of the fibers, while for composites with 30 and 40 vol% TVFs, there was activation of more complex mechanisms such as pullout, shearing, and fiber rupture. These results indicate that the TVF composite has great potential for use in bulletproof vests.

The main modifications of thermal and colorimetric parameters after thermal aging of DGEBA/TETA system (plain epoxy) and fique-fiber woven fabric-reinforced epoxy composites are described. As a preliminary study, thermal analysis was carried out on epoxy matrix composites reinforced with 15, 30, 40 and 50% fique-fiber woven fabric. After this previous analysis, the 40% composite was chosen to be thermally aged, at 170 °C. Three exposure times were considered, namely, 0, 72, 120 and 240 h. Samples were studied by thermogravimetric analysis (TGA), differential thermal analysis (DTA), differential scanning calorimetry (DSC), thermomechanical analysis (TMA) and colorimetry analysis. Significant color changes were observed after thermal aging combined with oxidation. It was also found that the thermal behavior of the plain epoxy showed greater resistance after thermal exposure. By contrast, the composites were more sensitive to temperature variations as a result of thermal stresses induced between fique fibers and the epoxy matrix.