Soldering processes are applied in the fabrication of electronic circuits used in most modern domestic and industrial technologies. This article aims to introduce a new soldering technology based on the microwave joining of copper materials used in electronic applications. The study was focused on microwave technology used as the thermal source for soldering. A simulation model of temperature distributions in copper plates with overall dimensions of 50 × 10 × 0.8 mm was developed in order to determine the necessary microwave power for soldering. For 270 °C simulated on the surface of copper plates, the microwave-injected power was determined to be 598.89 W. An experimental program for 600, 650, 700, and 750 W was set in order to achieve soldering of copper plates in less than 1 min. Soldered copper plates were subject to electrical resistance measurements being obtained with variations up to ±1.5% of the initial electrical resistance of the base materials. The quality of joints has also been analyzed through microscopy after the soldering process. In addition, mechanical properties were determined using a universal testing machine. The results have shown similar behavior of the samples layered with SAC on the one-side and double-side but also a significantly lower force before breaking for one-side-layered samples. An economic analysis was performed and the results obtained have shown that in terms of energy efficiency and total costs for microwave soldering compared with manual soldering, microwave soldering is cost-effective for industrial processing.

Thermal runaway in microwave hybrid heating of ceramics is an unwanted phenomenon which damages the sintered products. The aim of the present study is to establish to what extent the pressing forces of 100, 200 and 300 MPa used in the compaction process and the optimization of the microwave heating mechanism can reduce the occurrence of thermal runaway. Modeling and simulation of temperature distributions alongside defects created by the compaction process are performed in order to evaluate their influence on the stability of MHH. Based on CT scanning, defects with dimensions from 110 to 515 μm are studied in terms of local overheating and how the thermal runaway can lead to internal arc discharge. The results show that samples compacted at 100 MPa and exposed at 600 W injected power reach temperatures peaks around 1010 °C and are affected by major cracks and large melted areas. The samples compacted at 200 and 300 MPa present similar behavior, without arc discharge, but are also affected by cracks. Based on these findings, the MHH process can be applied to sintering processes but with a reduced injected power below 300 W for samples compacted with pressing forces higher than 300 MPa.

Over 60% of reported failures for reactive power compensation systems are given for damage to electrical circuit breaker contacts. This paper presents a study on the development of microwave technology for sintering of W–Cu–Cr alloys at 1012 °C for 65 min using 623.38 W microwave power, as well as microwave joining at 231 °C of the W–Cu–Cr composite material on body contact using 475 W microwave power for 55 s. The joined components were subjected to mechanical and electrical tests in accordance with ICE standards to validate the applied technology. Tests of connection–disconnection of the electrical contacts were carried out in accordance with the maximum number of disconnections allowed by the manufacturer (2 cycles/min): 25 s rest time and 5 s operating time under load. The components of the electrical contact after 111237 switches were analyzed under a microscope revealing a reduction of the damaged area by 27% compared with the original contact.

Magnesium-based alloys remain poorly researched, particularly regarding their behavior and resistance under hydrodynamic loading conditions. Interest in these materials is driven by their low density, lower even than that of aluminum alloys, and their excellent pressure die-casting capability, leading to manufacturing components with high geometric accuracy and structural homogeneity. Due to their biodegradability and biocompatibility, recent research has focused on using them in reconstructive surgery devices, similar to Zn-Mg alloys. As the blood circulatory system can, at certain stages, be considered similar to a hydraulic system, it is subjected to hydrodynamic flow regimes, including cavitation erosion. In this context, the current research, conducted on the AM50 magnesium-based alloy, provides new insights into its behavior and structural resistance exposed to shock waves and microjets generated by cavitation. Cavitation tests were performed using a standard 20 kHz vibratory device on three material conditions: one semi-finished (initial) state and two aged, heat-treated states at 200 °C for 12 and 24 h. Analyses of the characteristic erosion curves, cavitation resistance parameters, and macro- and microstructural examinations of the eroded surfaces revealed that, compared with the semi-finished condition, the applied heat-treatment regimes increased the HV₅ hardness by 6.8–17% and the cavitation resistance by 27–61%.

Altering the heating regime of the polymer during the fused filament fabrication (FFF) process can lead to changes in both the behaviour of the polymer and the characteristics of the printed product. This study proposes replacing the traditional resistive heating system with two hybrid systems that introduce an additional temperature of 120–160 °C: one combining resistive and hot air jet heating, and the other combining resistive and infrared radiation heating. The samples printed using these hybrid systems were analysed using differential scanning calorimetry (DSC) and visually inspected. Commercial ABS and PLA filaments were used in the experimental programme. A model to evaluate the polymer’s melting during the printing process was proposed and experimentally validated. Visual testing revealed that the printed lattice structure had smaller voids, characterised by depositions that were flattened rather than circular in cross-section due to the extended time in a viscous/partially molten state. The elongation viscosity and storage modulus decreased by approximately 10%, with a slightly smaller decrease observed for the infrared radiation heat source. The glass transition temperature remained unchanged, and the molecular mobility was not affected by the additional heat. Similarly, the energy required for crystal formation was unaffected by the supplementary heat. The mechanical behaviour of the printed pieces during compression tests was also influenced by the addition of a second heat source. For both materials, a decrease in deformability was observed as the temperature of the hot air jet increased.

This study investigates laser transmission welding of 30% glass fiber-reinforced polybutylene terephthalate (PBT-GF30). Injection-molded plates were used as base material, from which specimens were prepared, welded, and experimentally tested. The influence of key process parameters, including laser power, beam size, and scanning speed, on weld quality was systematically evaluated through an iterative optimization approach. An optimized parameter set (400 W laser power, reduced beam size, and increased scanning speed) enabled stable and repeatable weld formation with minimal thermal degradation. Experimental results were further supported by finite element analysis, showing good agreement between numerical and experimental data. The findings confirm the feasibility of laser welding for PBT-GF30 and its potential for aerospace applications requiring precision, weight reduction, and structural reliability.