Volatile organic compound (VOC) abatement has become imperative nowadays due to their harmful effect on human health and on the environment. Catalytic oxidation has appeared as an innovative and promising approach, as the pollutants can be totally oxidized at moderate operating temperatures under 500 °C. The most active single oxides in the total oxidation of hydrocarbons have been shown to be manganese and cobalt oxides. The main factors affecting the catalytic performances of several metal-oxide catalysts, including CoO_x and MnO_x, in relation to the total oxidation of hydrocarbons have been reviewed. The influence of these factors is directly related to the Mars–van Krevelen mechanism, which is known to be applied in the case of the oxidation of VOCs in general and hydrocarbons in particular, using transitional metal oxides as catalysts. The catalytic behaviors of the studied oxides could be closely related to their redox properties, their nonstoichiometric, defective structure, and their lattice oxygen mobility. The control of the structural and textural properties of the studied metal oxides, such as specific surface area and specific morphology, plays an important role in catalytic applications. A fundamental challenge in the development of efficient and low-cost catalysts is to choose the criteria for selecting them. Therefore, this research could be useful for tailoring advanced and high-performance catalysts for the total oxidation of VOCs.

This work presents the synthesis of nanostructured TiO₂ modified with noble metal nanoparticles (Au, Ag) and lysozyme and coated on titanium foil. Moreover, the specific structural and functional properties of the resulting inorganic and hybrid materials were explored. The purpose of this study was to identify the key parameters for developing engineered coatings on titanium foil appropriate for efficient dental implants with intrinsic antibacterial activity. TiO₂ nanoparticles obtained using the sol–gel method were deposited on Ti foil and modified with Au/Ag nanoparticles. Morphological and structural investigations (scanning electron and atomic force microscopies, X-ray diffraction, photoluminescence, and UV–Vis spectroscopies) were carried out for the characterization of the resulting inorganic coatings. In order to modify their antibacterial activity, which is essential for safe dental implants, the following aspects were investigated: (a) singlet oxygen (¹O₂) generation by inorganic coatings exposed to visible light irradiation; (b) the antibacterial behavior emphasized by titania-based coatings deposited on titanium foil (TiO₂/Ti foil; Au–TiO₂/Ti foil, Ag–TiO₂/Ti foil); (c) the lysozyme bioactivity on the microbial substrate (Micrococcus lysodeicticus) after its adsorption on inorganic surfaces (Lys/TiO₂/Ti foil; Lys/Au–TiO₂/Ti foil, Lys/Ag–TiO₂/Ti foil); (d) the enzymatic activity of the above-mentioned hybrids materials for the hydrolysis reaction of a synthetic organic substrate usually used for monitoring the lysozyme biocatalytic activity, namely, 4-Methylumbelliferyl β-D-N,N′,N″-triacetylchitotrioside [4-MU-β- (GlcNAc)₃]. This was evaluated by identifying the presence of a fluorescent reaction product, 7-hydroxy-4-metyl coumarin (4-methylumbelliferone).

We have explored an efficient strategy to enhance the overall photocatalytic performances of layered perovskites by increasing the density of hydroxyl group by protonation. The experimental procedure consisted of the slow replacement of interlayer Rb⁺ cation of RbLaTa₂O₇ Dion-Jacobson (DJ) perovskite by H⁺ via acid treatment. Two layered perovskites synthesized by mild (1200 °C for 18 h) and harsh (950 and 1200 °C, for 36 h) annealing treatment routes were used as starting materials. The successful intercalation of proton into D-J interlayer galleries was confirmed by FTIR spectroscopy, thermal analyses, ion chromatography and XPS results. In addition, the ion-exchange route was effective to enlarge the specific surface area, thus enhancing the supply of photocharges able to participate in redox processes involved in the degradation of organic pollutants. HLaTa_01 protonated layered perovskite is reported as a efficient photocatalyst for photomineralization of trichloroethylene (TCE) to Cl⁻ and CO₂ under simulated solar light. The enhanced activity is attributed to combined beneficial roles played by the increased specific surface area and high density of hydroxyl groups, leading to an efficiency of TCE mineralization of 68% moles after 5 h of irradiation.

The effect of gel preparation and heat treatment on the structural and optical properties of SiO₂-ZnO materials prepared by the sol–gel method was investigated. Zinc acetate dehydrate, TEOS (tetraethylortosilicate), ethanol, distillated water and HCl were used as a starting material, solvent and catalyst, respectively. Four powders (G1–G4) were prepared in different ways from the starting materials mentioned above. The method of adding Zn precursors during the synthesis differed from one another. For the G1 synthesis, only Zn acetate powder was employed; for the G2 synthesis, Zn acetate was dissolved in distilled water; and for the G3 synthesis, Zn acetate was dissolved in ethanol. When synthesizing G4, TEOS was added last, after Zn acetate had been combined with water and ethanol. The SiO₂-ZnO materials were dried at 200 °C and then heat-treated at 700 °C and 900 °C. All samples were investigated by X-ray diffraction and infrared spectroscopy in order to investigate their structure. SEM measurements were performed to investigate the morphology of materials. Optical properties were influenced by gel preparation and heat treatments. A reflectance of over 60% was obtained for G3 and G4 powders, while for G1 and G2, the reflectance was below 30%. In conclusion, synthesis steps and heat treatment can control the structure and properties of the powders.

Nanocomposites containingTiO₂ and activated carbon were obtained by the sol-gel method in the presence of Brij 58 surfactant. The sample with a higher surface area (185.6 m²/g) was promoted with Fe by impregnating it with aqueous solution of Fe(NO₃)₃. The obtained iron loadings, measured using X-ray fluorescence, were 0.83%, 3.30% and 7.17%. TiO₂ anatase was identified in all the samples by X-ray diffraction and Raman spectroscopy, but the presence of iron oxides could not be detected. However, infrared spectroscopy indicated the existence of Fe-O and Fe-O-Ti bonds. X-ray photoelectron spectroscopy revealed the presence of Fe²⁺ for samples with a lower Fe content and a mixture of Fe²⁺ and Fe³⁺ in the sample with 7.17% Fe. UV-Vis and photoluminescence spectroscopy showed the presence of carbon and Fe alongside TiO₂. This combination led to new properties due to the generation of intermediate energy levels and defects, contributing to an enhancement in the photocatalytic performance. The highest photodegradation efficiency of Congo red in solution (84.46%) was obtained for the sample with 7.17% Fe under visible light irradiation and acidic conditions. The synergistic contribution of dye adsorption and photodegradation was demonstrated, taking into account ZPC values of nanocomposites. Kinetic studies were completed with reaction mechanisms based on the results obtained in the presence of scavengers.

In this paper, we conducted a fundamental study concerning the effect of thermal treatment on the structure and morphology of 2 mol% vanadium doped ZnO nanopowders obtained by microwave assisted sol–gel method (MW). The samples were analyzed by DTA, FTIR, XRD, SEM, and UV–Vis spectroscopy. The DTA results showed that above 500 °C, there was no mass loss in the TG curves, and ZnO crystallization occurred. The XRD patterns of the thermally treated powders at 500 °C and 650 °C showed the crystallization of ZnO (zincite) belonging to the wurtzite-type structure. It was found that in the 650 °C thermally treated powder, aside from ZnO, traces of Zn₃(VO₄)₂ existed. FTIR spectra of the annealed samples confirmed the formation of the ZnO crystalline phase and V–O bands. The micrographs revealed that the temperature influenced the morphology. The increase in the annealing temperature led to the grain growth. The SEM images of the MW powder thermally treated at 650 °C showed two types of grains: hexagonal grains and cylindrical nanorods. UV–Vis spectra showed that the absorption band also increased with the increasing temperature of thermal treatment. The MW sample annealed at 650 °C had the highest absorption in ultraviolet domain.