Three Co-Cr alloy types (Co-Cr-Mo, Co-Cr-W, and Co-Cr-Mo-W) have been commonly used in the fabrication of dental prostheses. These alloys can be manufactured using either conventional casting or selective laser melting (SLM) techniques. Nevertheless, research that directly compares these materials and/or manufacturing processes in terms of their microstructural and mechanical characteristics is sparse. The purpose of this in vitro study was to conduct microstructural and mechanical analysis via X-ray interpretation, optical microscopy, scanning electron microscopy/energy dispersive X-ray spectroscopy (SEM/EDS), image analysis, X-ray diffraction (XRD), instrumented indentation testing (IIT), and 3-point bending testing to characterize Co-Cr-Mo, Co-Cr-W, and Co-Cr-Mo-W alloys produced through conventional casting and SLM. Six Co-Cr-based alloys were analyzed and divided into 3 types based on their elemental composition (Co-Cr-Mo, Co-Cr-W, and Co-Cr-Mo-W). Additionally, each group was categorized based on the manufacturing process used (casting or SLM). X-ray scans were used to assess porosity. The microstructures of the specimens were assessed through SEM/EDS examination and XRD analysis. IIT was used to determine the Martens hardness (HM) and elastic index (η_IT), while the elastic modulus (E) was estimated through the 3-point bending test. The mechanical properties were statistically analyzed using 2-way analysis of variance (ANOVA) and the Tukey multiple comparison post hoc test, with alloy type and manufacturing process as discriminating variables (α=.05). All cast groups exhibited gross porosity, while no pores or other flaws were found in the SLM groups. Based on the XRD results, the crystalline structure of all Co-Cr specimens consisted of the face-centered cubic γ phase (γ-fcc), along with the hexagonal close-packed ε phase (ε-hcp) and Cr₂₃C₆ carbide. Different microstructures were identified between the cast and SLM alloys. Significant differences were identified for the mean standard deviation HM (ranging from 2601 ±94 N/mm² to 3633 ±61 N/mm²) and mean ±standard deviation η_IT (ranging from 16.8 ±0.3% to 20.9 ±0.3%) among alloys prepared by the same manufacturing process, while all SLM alloys had statistically higher HM and η_IT results than their cast counterparts (P<.05). No statistically significant differences were identified for the mean ±standard deviation E_b (ranging from 170 ±25 GPa to 244 ±36 GPa) among the groups prepared with the same manufacturing process (P>.05), but the SLM alloys had significantly higher results (P<.05) than the cast alloys. In general, the manufacturing procedure significantly affected the porosity, microstructure, and mechanical properties of the tested Co-Cr alloys. SLM decreased the internal porosity, provided a uniform microstructure, and improved the mechanical properties for all the tested alloy types.

Background: One of the crucial factors influencing the longevity of anterior aesthetic dental restorations is the colour stability of resin composites. Bleaching and whitening have become popular methods for enhancing dental aesthetics. Home whitening techniques, such as special pens, are widely available commercially. This in vitro study aimed to determine the efficiency of a whitening pen in removing tea stains from resin composite by measuring colour differences (ΔE₀₀). Additionally, the study aimed to evaluate the variations in colour parameters measured by extra-oral and intra-oral spectrophotometers. Methods: A total of 45 disc-shaped resin composite specimens were randomly divided into three groups; Group 1: stored in artificial saliva (control), Group 2: stored in artificial saliva followed by a whitening pen application, and Group 3: stored in tea followed by a whitening pen application. Colour measurements were taken three times for each specimen using two spectrophotometers (extra-oral and intra-oral devices); T1: before storage (baseline), T2: after storage in artificial saliva or tea for 6 days; and T3: after one week of whitening pen application in groups 2 and 3. The data were statistically analyzed using one-way ANOVA followed by the Tukey post hoc test (p ≤ 0.05). The independent sample t-test was also employed. The equation of CIEDE2000 (ΔE₀₀) was used to calculate the colour difference between the dry, as-prepared specimens (baseline), and those after storage or bleaching. The colour changes exceeding the acceptability threshold (∆E₀₀ = 1.8) were considered unacceptable. Results: After whitening, the colour of the specimens stored in brewed tea (Group 3) remained unacceptable, as indicated by both the extra-oral and intra-oral spectrophotometers (ΔE₀₀ = 4 and 2.9, respectively). Groups 1 and 2 exhibited lower ΔE₀₀ values than Group 3 (p = 0.01 *). No significant difference was observed between Group 1 (stored in artificial saliva) and Group 2 (stored in artificial saliva and then bleached) (p = 0.3). Significant differences were consistently observed between the data obtained from the extra-oral spectrophotometer and the intra-oral one. Conclusions: The whitening pen proved ineffective in removing tea stains from resin composites. Although significant differences were found between the values obtained by the two spectrophotometers (extra-oral and intra-oral), both devices confirmed the unacceptable colour of the tea-stained resin composites after whitening.

Background and objectives: Even with the demand for high esthetics, the strength of the material for esthetic applications continues to be important. In this study, monolith zirconia (MZi) crowns fabricated using CAD/CAM were tested for fracture resistance (FR) in teeth with class II cavity designs with varying proximal depths, restored through a deep marginal elevation technique (DME). Materials and Methods: Forty premolars were randomly divided into four groups of ten teeth. In Group A, tooth preparation was conducted and MZi crowns were fabricated. In Group B, mesio-occluso-distal (MOD) cavities were prepared and restored with microhybrid composites before tooth preparation and the fabrication of MZi crowns. In Groups C and D, MOD cavities were prepared, differentiated by the depth of the gingival seat, 2 mm and 4 mm below the cemento-enamel junction (CEJ). Microhybrid composite resin was used for DME on the CEJ and for the restoration of the MOD cavities; beforehand, tooth preparations were conducted and MZi crowns were and cemented using resin cement. The maximum load to fracture (in newtons (N)) and FR (in megapascals (MPa)) were measured using the universal testing machine. Results: The average scores indicate a gradual decrease in the load required to fracture the samples from Groups A to D, with mean values of 3415.61 N, 2494.11 N, 2108.25 N and 1891.95 N, respectively. ANOVA revealed highly significant differences between the groups. Multiple group comparisons using the Tukey HSD post hoc test revealed that Group D had greater DME depths and showed significant differences compared with Group B. Conclusions: FR in teeth decreased when more tooth structure was involved, even with MZi crowns. However, DME up to 2 mm below the CEJ did not negatively influence the FR. Strengthening the DME-treated teeth with MZi crowns could be a reasonable clinical option, as the force required to fracture the samples far exceeded the maximum recorded biting force for posterior teeth.

Objective: The objective of this study was to evaluate the effect of different surface treatment methods on the shear bond strength (SBS) of metal brackets bonded to two types of CAD/CAM composite restorations: milled and 3D-printed. Materials and Methods: A total of 160 flat-shaped specimens (10 × 10 × 2 mm³) were prepared from four different CAD/CAM composites; two milled (Lava Ultimate™ [LU] and Grandio™ [GR]) and two 3D-printed (Crowntec™ [CT] and C&B Permanent™ [CB]). These specimens underwent thermocycling (5000 cycles at 5–55 °C), then were categorized based on the surface treatment into four groups (n = 10): Group C (control, no surface treatment), Group HF (treated with 9.6% hydrofluoric acid), Group DB (mechanical roughening by a diamond bur), and Group SB (sandblasting using aluminum oxide). Metal brackets were bonded using Transbond XT Primer and universal adhesive, stored in artificial saliva for 24 h, then thermocycled again. Shear bond strength (SBS) was tested using a universal testing machine until bracket debonding occurred. The adhesive remnant index (ARI) was assessed using a stereomicroscope to quantify the residual adhesive following debonding. Result: Regarding material, GR and LU restorations had significantly higher SBS values compared to CT and CB, ranging from 13.90 MPa to 20.35 MPa. Regarding surface treatment, SB and HF groups showed significantly higher SBS values. The ARI scores showed different adhesive modes of failure, with higher instances of scores 0 and 1, which indicate no or minimal adhesive remaining. Conclusions: Both milled and 3D-printed materials had adequate SBS for clinical use, with milled materials showing superior results. Surface treatments like sandblasting and HF significantly improved bond strength, with adhesive failure being common.

Objective: To evaluate the effect of different surface treatment methods on the shear bond strength (SBS) of metal brackets bonded to two types of CAD/CAM composite restorations: milled and 3D-printed. Materials and Methods: A total of 160 flat-shaped specimens (10×10×2 mm³) were prepared from four different CAD-CAM composites; two milled (Lava Ultimate™ [LU], and Grandio™ [GR]) and two 3D-printed (Crowntec™ [CT] and C&B Permanent™ [CB]). These specimens underwent thermocycling (5000 cycles at 5-55 °C), then were categorized based on the surface treatment into four groups (n=10): Group C (control, no surface treatment), Group HF (treated with 9.6 % hydrofluoric acid), Group DB (mechanical roughening by a diamond bur), and Group SB (sandblasting using aluminum oxide). Metal brackets were bonded, stored in artificial saliva for 24 hours, then thermocycled again. Shear bond strength (SBS) was tested using a universal testing machine until bracket debonding occurred. The adhesive remnant index (ARI) was assessed using a stereomicroscope to quantify the residual adhesive following debonding. Result: Regarding material, GR and LU restorations had significantly higher SBS values compared to CT and CB, ranging from 13.90 MPa to 20.35 MPa. Regarding surface treatment, SB and HF groups showed significantly higher SBS values. The ARI scores showed different adhesive modes of failure, with higher instances of scores 0 and 1 which indicate no or minimal adhesive remaining. Conclusion: Both milled and 3D-printed materials had adequate SBS for clinical use, with milled materials showing superior results. Surface treatments like sandblasting and HF significantly improved bond strength, with adhesive failure being common.