In many industries, polymers are in great demand due to their low weight and good mechanical properties. However, films and coatings are sometimes applied to improve polymer surface properties. This work presents a study on the metallisation of polycarbonates using a low pressure cold spray (LPCS) method. Two types of commercial powders were selected for the deposition of coatings: (i) tin and (ii) aluminium. The coatings were applied (i) on an unmodified substrate and (ii) on a substrate with an interlayer, which enabled the formation of good adherent aluminium coatings. A light and scanning microscopy was used to analyse the microstructure of coatings. Electrical conductivity was determined using the four-probe method and is discussed in relation to the oxygen content. Moreover, bond strength and microhardness were investigated.

This study investigates the mechanical properties and biocompatibility of eight commercially available filaments tailored for Fused Deposition Modeling (FDM) additive manufacturing. Test specimens were fabricated using original PRUSA MK4 printers, with ten samples from each selected polymer. Mechanical evaluations through static tensile and three-point bending tests revealed that PETG Carbon and PA+15CF exhibited superior tensile and flexural strengths, making them highly suitable for applications requiring high mechanical resilience. Biocompatibility assessments in line with the ISO 10993-5:2009 and ISO 10993-12:2021 standards indicated that all materials except FiberFlex 40D Fiberlogy were non-cytotoxic, supporting their potential in biomedical applications. The experimental data established material constants within the Johnson–Cook strength model, which effectively predicted the mechanical behaviors of monotonic materials like FiberFlex 40D, PETG, HIPS, TPU, and PA+15CF Rosa 3D, with maximum fitting errors not exceeding 2.6%. However, the model was inadequate for non-monotonic materials like PLA and PETG, resulting in higher errors and less accurate simulations. Scanning electron microscope (SEM) analyses provided insights into fracture mechanisms, correlating fracture surface characteristics with mechanical performance. This comprehensive study advances the understanding of mechanical properties in thermoplastic materials for 3D printing, validates numerical models for certain materials, and confirms material suitability for biomedical use.

In this study, the authors performed a strength analysis of seven groups of commercially available materials based on SLS incremental technology. Test samples were made with Original PRUSA SL1S printers, with 10 samples of each type from 7 resins selected for testing. The tests were carried out on an MTS Bionix machine in a static tensile test, during which the basic mechanical properties were determined. This is also a preliminary study to determine material constants in the Johnson-Cook strength model. The authors then performed numerical simulations to mirror the experimental tests in order to tune the rheological model. In addition, a fracture criterion was determined based on a hybrid FEM/SPH numerical method. This allowed for the expansion of material libraries currently used in numerical simulations, as well as the sensitivity of the materials’ models. In subsequent studies, in order to determine the nature of material destruction, analysis of fracture surfaces was performed using a scanning electron microscope (SEM). The final study was a biocompatibility test to assess the biological properties of the material. The conducted research made it possible to determine the strength properties of resins currently used in 3D printers, expand the libraries of material models in the computational environment (with an error rate of less than 5%), as well as observe the nature of the cracks formed and biocompatibility in the context of predicting the use of these materials for biomedical applications.

The paper presents results of a research on identifying opportunities for effective reclamation of waste molding sand with water-glass, hardened by microwave heating. The molding sand applied in the tests was prepared with use of selected type 145 of sodium water-glass. The sand was sequentially processed by microwave hardening, cooling, thermal loading to 800°C, cooling to ambient temperature, crushing and mechanical reclamation. These stages create a closed processing loop. After each cycle, changes of tensile strength and bending strength were determined. Results of the study show that it is possible to activate surface of high-silica grains of waste foundry sand hardened with microwaves, provided that applied are appropriate processing parameters in successive operation cycles.