Thanks to the continuous development of light-curing resin composites it is now possible to print permanent single-tooth restorations. The purpose of this study was to compare resin composites for milling -Gandio Blocks (GR), Brilliant Crios (CR) and Enamic (EN) with resin composite for 3D printing—Varseo Smile Crown plus (VSC). Three-point bending was used to measure flexural strength (σ_f) and flexural modulus (E_f). The microhardness was measured using a Vickers method, while fractographic, microstructural, texture and fractal dimension (FD) analyses were performed using SEM, optical microscope and picture analysis methods. The values of σ_f ranged from 118.96 (±2.81) MPa for EN to 186.02 (±10.49) MPa for GR, and the values of E_f ranged from 4.37 (±0.8) GPa for VSC to 28.55 (±0.34) GPa for EN. HV01 ranged from 25.8 (±0.7) for VSC to 273.42 (±27.11) for EN. The filler content ranged from 19–24 vol. % for VSC to 70–80 vol. % for GR and EN. The observed fractures are typical for brittle materials. The correlation between FD of materials microstructure and E_f was observed. σ_f of the printed resin depends on layers orientation and is significantly lower than σ_f of GR and CR. E_f of the printed material is significantly lower than E_f of blocks for milling.

Nowadays, the replacement of a hip joint is a standard surgical procedure. However, researchers have continuingly been trying to upgrade endoprostheses and make them more similar to natural joints. The use of 3D printing could be helpful in such cases, since 3D-printed elements could mimic the natural lubrication mechanism of the meniscus. In this paper, we propose a method to deposit plastics directly on titanium alloy using 3D printing (FDM). This procedure allows one to obtain endoprostheses that are more similar to natural joints, easier to manufacture and have fewer components. During the research, biocompatible polymers suitable for 3D FDM printing were used, namely polylactide (PLA) and polyamide (PA). The research included tensile and shear tests of metal–polymer bonds, friction coefficient measurements and microscopic observations. The friction coefficient measurements revealed that only PA was promising for endoprostheses (the friction coefficient for PLA was too high). The strength tests and microscopic observations showed that PLA and PA deposition by 3D FDM printing directly on Ti6Al4V titanium alloy is possible; however, the achieved bonding strength and repeatability of the process were unsatisfactory. Nevertheless, the benefits arising from application of this method mean that it is worthwhile to continue working on this issue.

The paper presents the results of tests of a welded joint of Hardox 450 steel, belonging to the group of weldable high-strength boron steels with increased resistance to abrasive wear. As a result of the conducted research, apart from the basic structural indicators, an attempt was made to determine the correlation between the grain size of the prior austenite in the characteristic weld zones and its basic mechanical properties, such as yield point, tensile strength, percentage elongation after fracture, reduction of area, and impact strength. The scope of research quoted above was carried out for a welded joint of the considered steel at delivery state (directly after welding), in the normalising annealed state, as well as in water-quenched state, using different austenitisation temperatures in the range of 900–1200 °C. The results obtained showed a large influence of the parameters of the applied thermal heat treatment on the selected structural and mechanical properties of the welded joint.

This study investigates the mechanical properties and biocompatibility of eight commercially available filaments tailored for Fused Deposition Modeling (FDM) additive manufacturing. Test specimens were fabricated using original PRUSA MK4 printers, with ten samples from each selected polymer. Mechanical evaluations through static tensile and three-point bending tests revealed that PETG Carbon and PA+15CF exhibited superior tensile and flexural strengths, making them highly suitable for applications requiring high mechanical resilience. Biocompatibility assessments in line with the ISO 10993-5:2009 and ISO 10993-12:2021 standards indicated that all materials except FiberFlex 40D Fiberlogy were non-cytotoxic, supporting their potential in biomedical applications. The experimental data established material constants within the Johnson–Cook strength model, which effectively predicted the mechanical behaviors of monotonic materials like FiberFlex 40D, PETG, HIPS, TPU, and PA+15CF Rosa 3D, with maximum fitting errors not exceeding 2.6%. However, the model was inadequate for non-monotonic materials like PLA and PETG, resulting in higher errors and less accurate simulations. Scanning electron microscope (SEM) analyses provided insights into fracture mechanisms, correlating fracture surface characteristics with mechanical performance. This comprehensive study advances the understanding of mechanical properties in thermoplastic materials for 3D printing, validates numerical models for certain materials, and confirms material suitability for biomedical use.

In this study, the authors performed a strength analysis of seven groups of commercially available materials based on SLS incremental technology. Test samples were made with Original PRUSA SL1S printers, with 10 samples of each type from 7 resins selected for testing. The tests were carried out on an MTS Bionix machine in a static tensile test, during which the basic mechanical properties were determined. This is also a preliminary study to determine material constants in the Johnson-Cook strength model. The authors then performed numerical simulations to mirror the experimental tests in order to tune the rheological model. In addition, a fracture criterion was determined based on a hybrid FEM/SPH numerical method. This allowed for the expansion of material libraries currently used in numerical simulations, as well as the sensitivity of the materials’ models. In subsequent studies, in order to determine the nature of material destruction, analysis of fracture surfaces was performed using a scanning electron microscope (SEM). The final study was a biocompatibility test to assess the biological properties of the material. The conducted research made it possible to determine the strength properties of resins currently used in 3D printers, expand the libraries of material models in the computational environment (with an error rate of less than 5%), as well as observe the nature of the cracks formed and biocompatibility in the context of predicting the use of these materials for biomedical applications.

Hadfield steel, under unit pressure conditions, strengthens itself by forming a high density dislocation structure, which results in increased resistance to dynamic impact wear. However, under abrasion conditions, the homogeneous microstructure of the cast steel is insufficient to achieve the expected service life. The aim of the research is to conduct a comparative analysis of the material in its as-delivered state and after two-stage heat treatment (isothermal annealing followed by re-austenitisation). It was found that after isothermal annealing of X120Mn12 grade steel at a temperature of 510 °C, a microstructure with a complex morphology consisting of colonies of fine-grained pearlite, (Fe,Mn)₃C carbides distributed along the grain boundaries of the former austenite and needle-like (Fe,Mn)₃C carbides was obtained in the austenite matrix. The subsequent thermal treatment of the steel with the use of supersaturating annealing at 900 °C resulted in a heterogeneous microstructure consisting of evenly distributed globular carbide precipitations in a matrix of considerably finer austenite grains in comparison with the as-delivered original state. As a result of the final microstructural changes achieved, a 16.4% increase in abrasion resistance was obtained compared to the delivered condition.