The asphalt industry has long been challenged with finding sustainable solutions to enhance the performance of asphalt mixtures while mitigating their environmental impact. One promising avenue is the incorporation of waste filler materials into asphalt mixtures. This review explores the feasibility and effectiveness of utilizing waste filler in asphalt mixtures, focusing on its effects on the mechanical characteristics, durability, and sustainability of asphalt pavements. Various waste filler materials, such as rice husk ash, fly ash, and construction and demolition wastes, have been examined in terms of their potential as substitutes for traditional filler materials such as limestone and mineral powders. This review synthesizes literature to assess the impact of waste fillers on the performance of asphalt mixtures, including rutting resistance, fatigue behavior, moisture susceptibility, and aging characteristics. This work begins by examining the interaction of the asphalt fillers to provide clarification. The usage of various waste fillers is then examined. With fewer harmful environmental consequences than traditional cement manufacturing has, waste filler materials improve the strength and durability of asphalt mixtures. This research underscores the promising future of waste filler materials as environmentally friendly and innovative materials. To fully capitalize on their benefits, further research, standardization, and widespread use of waste filler-based products are necessary.

The use of hot mix asphalt (HMA) has several drawbacks, such as the emission of harmful gases into the atmosphere, difficulties in maintaining temperature over long distances, and the requirement for high energy consumption during preparation and installation. In order to solve these issues, this research aimed to produce High-Performance Cold Mix Asphalt (HP-CMA), in which Ordinary Portland Cement (OPC) is used as a filler to replace limestone filler at 0%, 1.5%, 3%, 4.5%, and 6% of the aggregate weight. Indirect Tensile Stiffness Modulus (ITSM), moisture susceptibility, temperature susceptibility, and microstructural analysis tests were carried out. The results showed that the ITSM was considerably enhanced when OPC was utilized. When comparing HP-CMA with 3% OPC to the control HMA (100–150 pen), the ITSM increased by approximately 80% after three days. In contrast, HP-CMA with 4.5% OPC achieved the same ITSM as the control HMA (40–60 pen) after seven days. Moreover, the ITSM of the HMA 40–60 pen decreased by 91.93% when the temperature rose from 20 °C to 45 °C, whereas the ITSM of the HP-CMA with 6% OPC decreased by 42.47% over the same temperature range. This suggests that HP-CMA is more stable than the HMA 40–60 pen at elevated temperatures. The superior performance of the HP-CMA can be attributed to two essential factors: the improved binding effect due to the demulsification of the asphalt emulsion used as a binder, and the formation of hydration products from the added cement.