Hot mix asphalt has various benefits such as good workability and durability. It is one of the most general materials used as asphalt mixtures in road pavements. Asphalt mixtures and binders can be improved by modifying them with various additives. Gilsonite is a natural asphalt hydrocarbon which may be used as an additive to hot mix asphalt. It is used as an asphalt binder modifier (wet process) and an asphalt mixture modifier (dry process) to improve the properties of the mix. It provides the option of improved rheological properties, stability, strength rutting resistance and moisture sensitivity. This paper examines the current research relating to the use of gilsonite to improve the asphalt properties (binder and mixture). The rheological properties of the modified asphalt binders and mechanical properties of the modified asphalt mixtures will be reviewed. The influence of adding gilsonite individually or combined with other additives will be discussed. Furthermore, assessment of the environmental and economic perspectives of the studied asphalt along with some suggestions to improve the asphalt binders and mixtures will be explored.

Conventional hot mix plants operate to support large paving projects, making production more economic with high volume output. When repairs and maintenance are needed, it can be challenging to maintain small quantities of hot bituminous mixtures at a sufficient temperature, especially in the case of winter maintenance. Consequently, the repair materials cannot be compacted to the desired level on some occasions. This research aimed to develop a polymer modified asphalt binder with reduced temperature sensitivity for hand-laid and low-volume applications. The results showed that the highest penetration index has been achieved by modifying bitumen with 20% rubber and 2% wax. The FTIR and XRD analysis indicated that the bitumen, rubber and wax that react chemically to build 3D networks have an interlocked structure in the bitumen matrix resulting in reduced temperature sensitivity of the polymer modified asphalt binder. Furthermore, indirect tensile stiffness, permanent deformation, creep test and fatigue life test, water sensitivity and freeze-thaw cycle demonstrated an improvement in the asphalt mixture properties in terms of mechanical and durability perspectives. Overall, based on this investigation, modifying asphalt binder with 20% rubber and 2% wax resulted in stronger and durable asphalt mixture in comparison to traditional hot mix asphalt.

Cold mix asphalt (CMA) is emerging as an environmentally friendly alternative to traditional hot mix asphalt (HMA). It offers advantages such as lower costs, reduced energy demands, decreased environmental impacts, and improved safety aspects. Among the various types of CMA, the cold bitumen emulsion mixture (CBEM) stands out. The CBEM involves diluting bitumen through emulsification, resulting in lower bitumen viscosity. However, this process has certain drawbacks, including extended setting (curing) times, lower early strength, increased porosity, and susceptibility to moisture. This study focuses on enhancing CBEM properties through the utilization of low-energy heat techniques, such as microwave technology, and the incorporation of a polymeric additive, specifically acrylic. These innovations led to the development of a novel paving technology known as a half-warm bitumen emulsion mixture (HWBEM). The research was conducted in two phases. First, the study assessed the impact of low-energy heating on the CBEM. Subsequently, it explored the combined effects of low-energy heating and the addition of an acrylic polymer. CBEM samples containing ordinary Portland cement (OPC) as an active filler were utilized in the sample manufacturing process. The effectiveness of these techniques in enhancing crack resistance was evaluated by analysing the results of the indirect tensile strength test. Notably, CBEM samples containing an amount of 2.5% of acrylic polymer and OPC exhibited the highest resistance to cracking. Furthermore, significant improvements were observed in their volumetric and mechanical properties, comparable to those of HMA.

This study explores the potential of calcium carbide residue (CCR) as an alternative activator for ground granulated blast-furnace slag (GGBS) to reduce reliance on ordinary Portland cement (OPC) in mortar production. A series of OPC-GGBS-CCR ternary binders were prepared and evaluated for their fresh and mechanical properties over various curing periods. The findings showed that mortars’ fresh and mechanical characteristics were significantly improved with longer curing times, suggesting CCR’s potential to efficiently activate GGBS, thereby benefiting the environment and economy. Significant enhancements in compressive strengths were observed after 7 days of curing, with increases of 44%, and 69–144% for OPC and OPC-GGBS-CCR ternary binders, respectively, while the utilization of activated binders led to flexural strength growth compared to three days of curing, with improvements of 70–173% for OPC-GGBS-CCR ternary binders, respectively. Microstructural analyses confirmed accelerated hydration and increased product formation due to CCR’s calcium content. An optimal mix ratio of OPC:GGBS:CCR = 1:1:0.5 demonstrated mechanical properties comparable to OPC mortars after 28 days, highlighting CCR’s potential for sustainable cementitious materials.

The use of hot mix asphalt (HMA) has several drawbacks, such as the emission of harmful gases into the atmosphere, difficulties in maintaining temperature over long distances, and the requirement for high energy consumption during preparation and installation. In order to solve these issues, this research aimed to produce High-Performance Cold Mix Asphalt (HP-CMA), in which Ordinary Portland Cement (OPC) is used as a filler to replace limestone filler at 0%, 1.5%, 3%, 4.5%, and 6% of the aggregate weight. Indirect Tensile Stiffness Modulus (ITSM), moisture susceptibility, temperature susceptibility, and microstructural analysis tests were carried out. The results showed that the ITSM was considerably enhanced when OPC was utilized. When comparing HP-CMA with 3% OPC to the control HMA (100–150 pen), the ITSM increased by approximately 80% after three days. In contrast, HP-CMA with 4.5% OPC achieved the same ITSM as the control HMA (40–60 pen) after seven days. Moreover, the ITSM of the HMA 40–60 pen decreased by 91.93% when the temperature rose from 20 °C to 45 °C, whereas the ITSM of the HP-CMA with 6% OPC decreased by 42.47% over the same temperature range. This suggests that HP-CMA is more stable than the HMA 40–60 pen at elevated temperatures. The superior performance of the HP-CMA can be attributed to two essential factors: the improved binding effect due to the demulsification of the asphalt emulsion used as a binder, and the formation of hydration products from the added cement.