Decompression or healing chambers between the threads have been proposed to improve and accelerate the osseointegration process of dental implants. The aim of the present work was to test, in an in vivo sheep study, if healing chambers between the threads could produce a better osseointegration process. Thirty titanium implants (15 conventional design (control) and 15 implants with healing chambers (test)) were inserted in a random fashion in the tibia of 3 sheep. The animals were euthanized after 30 days of healing, and the retrieved specimens treated to obtain thin ground sections. Histological observations showed that the quantity of newly formed bone growing in an apical direction was lower in the control group (1095 µm) when compared to the Test group (1658 µm). This difference was statistically significant. Moreover, a layer of osteogenic matrix was present around the portion of implants immersed in the marrow spaces. This osteogenic tissue was thicker in the test group. In conclusion, the present study confirmed the very good results in implants with healing chambers that presented a higher percentage of new bone formation.

Threads of dental implants with healing chamber configurations have become a target to improve osseointegration. This biomechanical and histometric study aimed to evaluate the influence of implant healing chamber configurations on the torque removal value (RTv), percentage of bone-to-implant contact (BIC%), bone fraction occupancy inside the thread area (BAFO%), and bone and osteocyte density (Ost) in the rabbit tibia after two months of healing. Titanium implants with three different thread configurations were evaluated: Group 1 (G1), with a conventional “v” thread-shaped implant design; Group 2 (G2), with square threads; and Group 3 (G3), the experimental group with longer threads (healing chamber). Ten rabbits (4.5 ± 0.5 kg) received three implants in each tibia (one per group), distributed in a randomized manner. After a period of two months, the tibia blocks (implants and the surrounding tissue) were removed and processed for ground sectioning to evaluate BIC%, BAFO%, and osteocyte density. The ANOVA one-way statistical test was used followed by the Bonferoni’s multiple comparison test to determine individual difference among groups, considering a statistical difference when p < 0.05. Histometric evaluation showed a higher BAFO% values and Ost density for G3 in comparison with the other two groups (G1 and G2), with p < 0.05. However, the RTv and BIC% parameters were not significantly different between groups (p > 0.05). The histological data suggest that the healing chambers in the implant macrogeometry can improve the bone reaction in comparison with the conventional thread design.

A new implant design with healing chambers in the threads was analyzed and compared with a conventional implant macrogeometry, both implants models with and without surface treatment. Eighty conical implants were prepared using commercially pure titanium (grade IV) by the company Implacil De Bortoli (São Paulo, Brazil). Four groups were performed, as described below: Group 1 (G1), traditional conical implants with surface treatment; group 2 (G2), traditional conical implants without surface treatment (machined surface); group 3 (G3), new conical implant design with surface treatment; group 4 (G4), new conical implant design without surface treatment. The implants were placed in the two tibias (n = 2 implants per tibia) of twenty New Zealand rabbits determined by randomization. The animals were euthanized after 15 days (Time 1) and 30 days (Time 2). The parameters evaluated were the implant stability quotient (ISQ), removal torque values (RTv), and histomorphometric evaluation to determine the bone to implant contact (%BIC) and bone area fraction occupancy (BAFO%). The results showed that the implants with the macrogeometry modified with healing chambers in the threads produced a significant enhancement in the osseointegration, accelerating this process. The statistical analyses of ISQ and RTv showed a significative statistical difference between the groups in both time periods of evaluation (p ≤ 0.0001). Moreover, an important increase in the histological parameters were found for groups G3 and G4, with significant statistical differences to the BIC% (in the Time 1 p = 0.0406 and in the Time 2 p < 0.0001) and the BAFO% ((in the Time 1 p = 0.0002 and in the Time 2 p = 0.0045). In conclusion, the result data showed that the implants with the new macrogeometry, presenting the healing chambers in the threads, produced a significant enhancement in the osseointegration, accelerating the process.

This study aims to evaluate the effects of implant macrogeometry on the early period of the osseointegration process, comparing four different implant models through biomechanical and histological analysis after implantation in rabbit tibiae. Twenty New Zealand rabbits were used, evaluated at two different times (21 and 28 days) after installation of the implant. Eighty implants with different macrogeometries were used, forming four groups (n = 20 per group): cylindrical implants Ø4.1 mm and 8 mm in length (STRc group); cylindrical-conical implants Ø4.1 mm and 8 mm in length (STRt group); tapered implants Ø4.3 mm and 8 mm in length (NOBt group); and tapered implants with healing chambers Ø4.0 mm and 8 mm in length (MAEt group). Ten samples from each group were analyzed at each proposed time. The initial implant stability quotient (ISQ) was measured by resonance frequency analysis, both at the time of installation and at the time of sacrifice. In the histological sections, the percentage of bone-implant contact (BIC%), newly formed bone, osteoid matrix, and medullary spaces were measured in the pre-determined cortical and medullary bone portion for each sample. The three tapered implant groups (STRt, NOBt, and MAEt) showed higher values for the analyzed parameters in the early osseointegration period, in comparison with the cylindrical implant group (STRc). In all parameters, the three tapered groups showed no difference (p > 0.05); however, all three tapered groups presented significant differences, when compared to the cylindrical group (p < 0.05). No correlation was detected between the parameters analyzed. Within the limitations of the present study, in all parameters analyzed, the tapered implants demonstrated greater results when compared to the cylindrical implants.

Background: The physicochemical changes of the surface aim to improve cell adhesion, proliferation, and differentiation, that is, better biological interaction with the cells and, consequently, with the peri-implant tissues. In the present study, implants with the same macrogeometry were compared in vitro and in vivo, but with two different surfaces: micro-rough and a new micro-nano-rough surface. Materials and Methods: A total of 90 implants were used, 10 of which were used for in vitro surface characterization (n = 5 per group) through scanning electron microscopy (SEM), atomic force microscopy (AFM), and surface roughness measurements. For in vivo tests, 80 implants (n = 40 per group) were used in 20 rabbits (n = 2 implants per tibia). Two experimental groups were created: a control group, where the implants had a surface treated by sandblasting with titanium oxide microparticles, and a test group, where the implants were sandblasted using the same process as the previous group plus acid conditioned. The implant stability quotient (ISQ) was measured by resonance frequency (initially and at both euthanasia times). Animals were euthanized 3 and 5 weeks after implantation (n = 10 animals per time). Ten samples from each group at each time point were evaluated by removal torque (RTv). Another ten samples from each group were evaluated histologically and histomorphometrically, measuring the percentage of bone-to-implant contact (%BIC) and the bone area fraction occupancy (%BAFO). Results: In vitro, it was possible to observe a more homogeneous surface for the test group compared to the control group. ISQ values showed statistical differences at both 3 and 5 weeks (test > control). For RTv, the values were: 44.5 ± 4.25 Ncm (control group) and 48.6 ± 3.17 Ncm (test group) for the time of 3 weeks; 64.3 ± 4.50 Ncm (control group) and 76.1 ± 4.18 Ncm (test group) at 5 weeks. The %BIC and %BAFO values measured in both groups and at both times did not show significant differences (p > 0.05). Conclusions: The higher removal torque and ISQ values presented in the samples from the test group compared to the control group indicate that there was an acceleration in the mineralization process of the newly formed bone matrix.

Objective: This study aimed to evaluate peri-implant tissue changes during early osseointegration using a combined approach of digital radiographic analysis, RGB pseudocolorization, and histomorphometry in a sheep tibia model. Materials and Methods: Thirty titanium implants were placed in the tibiae of six adult sheep and evaluated at 14 and 28 days post-implantation. Digital periapical radiographs were acquired, grayscale values and RGB channel intensities were measured using Fiji/ImageJ, and compared with histological parameters (bone tissue, collagen, and medullary spaces) quantified from picrosirius–hematoxylin-stained sections. Manual overlay of radiographic and histological images was performed to ensure spatial correspondence of regions of interest. Statistical analyses assessed differences over time and correlations between image data and histological composition. Results: Radiographic grayscale values and histologically measured bone and collagen increased significantly from 14 to 28 days (p < 0.01), while medullary spaces decreased (p < 0.001), indicating progressive bone formation and matrix maturation. RGB analysis revealed significant increases in green channel intensity and decreases in red channel intensity (p < 0.05), while the blue channel remained stable. At 14 days, strong correlations were observed between blue channel intensity and bone tissue (r = 0.81; p = 0.015), and between green channel intensity and collagen (r = 0.98; p < 0.001). Visual overlays demonstrated alignment between radiographic high-density zones and histologically dense bone regions. Conclusions: RGB pseudocolorized radiographic analysis, correlated with histological findings, offers a non-invasive and reproducible method for early detection of peri-implant tissue maturation. This feasibility correlation study provides a foundation for future investigations integrating imaging, histology, and biomechanical testing.