Carbodiimide (EDC)–based dentin primers preserve hybrid layer (HL) integrity. However, aging >1 y has not been investigated. The present study examined whether the cross-linking effect of EDC was reflected in dentin bond strength, endogenous enzymatic activity, and the chemical profile of the HL after 5-y aging in artificial saliva. Noncarious human third molars ( N = 42) were cut to expose middle/deep coronal dentin and treated as follows: group 1, dentin etched with 35% H₃PO₄, pretreated with a 0.3M aqueous EDC primer for 1 min and restored with XP Bond (Dentsply Sirona); group 2, as in group 1 but without EDC pretreatment; group 3, Clearfil SE Bond (Kuraray-Noritake) primer applied to dentin surface, followed by EDC pretreatment as in group 1 and application of bond; group 4, as in group 3 without EDC pretreatment. After composite buildup, the specimens were cut into sticks or slabs, depending on the experiment. All tests were performed at baseline (T0) and after 5 y of aging (T5) in artificial saliva at 37 °C. Microtensile bond strength (µTBS) was tested at a crosshead speed of 1 mm/min until failure. Endogenous enzymatic activity was investigated with in situ zymography. The chemical profile of HL was determined via Raman spectroscopy. Three-way analysis of variance and post hoc Tukey test were used to analyze µTBS and in situ zymography data (α = 0.05). EDC pretreatment and aging significantly influenced µTBS and in situ zymography results ( P < 0.05). Higher bond strength and lower gelatinolytic activity were identified in the EDC-treated groups at T5 ( P < 0.05), especially in the etch-and-rinse groups. Raman spectra revealed less defined amide III peaks in control specimens at T5. The EDC cross-linking effect persisted in the HL for 5 y in terms of bond strength, collagen structure preservation, and dentinal enzyme silencing.

Resin infiltration is a conservative treatment of initial enamel carious lesions. Only one infiltrant material is available on the market (Icon, DMG), and research is now investigating new chemical compositions so as to further exploit the benefits of the resin infiltration technique. A literature search of the articles testing the effects of different formulations on mechanical properties, resin penetration ability, remineralizing, and antibacterial activities was conducted. Of 238 articles, 29 resulted in being eligible for the literature review. The formulations investigated were all different and consisted in the inclusion of hydrophobic monomers (i.e., BisEMA, UDMA), solvents (ethanol, HEMA), alternative etchants (PAM) or molecules with antibacterial or bioactivity features (i.e., AgNP, YbF_3, MTZ, chitosan, DMAMM, HAp, MC-IL, NACP, PUA, CHX) and microfilled resins. Information on the long-term performances of the tested experimental materials were scarce. The combination of TEGDMA with hydrophobic monomers and the inclusion of a solvent alternative to ethanol reinforced mechanical properties of the materials. Hybrid-glass materials demonstrated an enhanced remineralization capacity. Techniques such as tunnelization increased the penetration depth and preserved the recourse to less-conservative treatments. Combining the min-invasive infiltrant approach with remineralizing and bacteriostatic properties would be beneficial for therapeutic and economical aspects, according to the principles of minimally invasive dentistry.

The effects of different finish line designs on the seating accuracy of partial indirect restorations are unclear. The purpose of this in vitro study was to evaluate the influence of different preparation designs on the marginal and internal discrepancy of lithium disilicate computer-aided design and computer-aided manufacture (CAD-CAM) partial indirect restorations before and after thermomechanical aging by using 3-dimensional (3D) microcomputed tomography (μCT). Forty human molars were divided according to the preparation design and their location relative to the tooth survey line: SO: rounded shoulder occlusal to the survey line; CO: chamfer occlusal to the survey line; SA: rounded shoulder apical to the survey line; CA: chamfer apical to the survey line (n=10). Ceramic onlays were luted using a universal resin cement (RelyX Universal + Scotchbond Universal Plus). The specimens underwent thermomechanical loading in a mastication simulator (1 200 000 mechanical and 5000 thermal cycles). The marginal and internal discrepancy was evaluated with μCT before and after aging. The volume of cement and internal voids was evaluated with 3-dimensional imaging. The marginal discrepancy (MD), absolute marginal discrepancy (AMD), axial gap (AG), and occlusal gap (OG) were quantified using 2-dimensional analyses. Data were statistically analyzed using a 2-way ANOVA and the Tukey post hoc test (α=.05). Preparation designs apical to the survey line resulted in a larger volume of cement compared with those occlusal to the survey line (P<.05). No differences were observed in the internal voids among the groups immediately or after aging (P>.05). Both preparation designs and aging had a significant influence on the MD, AMD, AG, and OG (P<.05). Specifically, CB exhibited significantly greater values for AMD, MD, AG, and OG compared with all other preparations (P<.05). CA and SA performed significantly worse than CO and SO in terms of AMD and MD (P<.005). Preparations located occlusal to the survey line, particularly CO, demonstrated superior results with respect to both marginal and internal adaptations. CA exhibited the least favorable adaptation among the preparations investigated. Aging had a detrimental impact on the marginal adaptation of the restorations, regardless of the specific preparation design used.

Background/Objectives: Osseointegration of titanium dental implants is essential for the long-term success of prosthetic treatments. Cold atmospheric pressure plasma (CAP) has recently emerged as a promising surface modification technique aimed at enhancing early osseointegration by improving implant surface properties and exerting antimicrobial effects. This systematic review aims to critically evaluate the in vivo preclinical evidence on the effects of CAP or similar cold plasma treatments on titanium dental implant surfaces with regard to osseointegration outcomes. Methods: A systematic literature search was conducted in PubMed and Scopus databases for preclinical in vivo studies published between 2005 and 2025 investigating the effects of cold plasma on titanium dental implant surfaces. The primary outcome assessed was the bone-to-implant contact (BIC), followed by secondary outcomes including implant stability quotient (ISQ), removal torque, bone area fraction occupancy (BAFO), peri-implant bone density (PIBD), interfacial bone density (IBD), bone-implant direct weight (BDWT) and bone loss measurements via histology and micro-CT. Risk of bias was evaluated using the SYRCLE Risk of Bias tool. Results: Nine eligible studies involving 310 titanium implants in 71 animal models (dogs, pigs and mice) were included. CAP-treated implants consistently demonstrated significant improvements in early osseointegration parameters compared to controls, with statistically significant increases in BIC (up to +20%), BAFO and biomechanical fixation metrics (removal torque and ISQ). Micro-CT analyses revealed enhanced peri-implant bone density and architecture. No adverse biological events or implant failures related to plasma treatment were reported. However, heterogeneity in plasma protocols, animal species and short follow-up durations (2–12 weeks) limited comparability and long-term interpretation. Conclusions: Preclinical evidence seems to support CAP as a safe and potentially effective surface treatment for enhancing early osseointegration of titanium dental implants. Further standardized long-term studies involving functional loading and clinical trials in humans are needed to confirm clinical efficacy and optimize treatment protocols.