Five different alloy hardfacings on 16MnCr5 grade low-carbon ferritic–pearlitic steel were investigated in terms of their abrasive wear resistance in laboratory testing conditions. The selected hardfacing materials, namely “E520 RB”, “RD 571”, “LNM 420FM”, “E DUR 600”, and “Weartrode 62”, were individually deposited onto plain ground-finish surfaces of 10 mm thick steel plate samples. The studied hardfacings were fabricated using several different welding methods and process parameters proposed by their industrial manufacturers. In the present comparative study, the results obtained from laboratory abrasive wear tests of the investigated hardfacings were analyzed and discussed in relation to their microstructure, hardness, and wear mechanism characteristics. Regardless of great variety in microstructure and chemical composition of individual hardfacing materials, the results clearly indicated the governing factor for the wear resistance improvement to be the overall carbon content of the used hardfacing material. Thus it has been shown that the “E520 RB” hardfacing exhibited the highest abrasive wear resistance thanks to its appropriate hardness and beneficial “ledeburite-type” eutectic microstructure.

Clinching is a manufacturing method of mechanically joining two or more materials without the use of heat or additional components. This process relies on high plastic deformation to create a secure bond. Clinching technology is widely used for joining materials of various grades and thicknesses. Especially in the automotive industry, clinching is an alternative to resistance spot welding. However, the load-bearing capacity of clinched joints is comparatively lower when compared to resistance spot-welded joints. This research aimed to increase the load-carrying capacity of clinched joints. To enhance the load-bearing capacity of the clinched joints, localized modification of the microstructure was carried out, primarily focusing on the neck area of the joint. The alteration of the microstructure within the clinched joint was accomplished through the application of localized heating using the resistance spot welding method. The microstructure distribution in the clinched joint region was analyzed using light and scanning electron microscopy, as well as microhardness measurements. Two material grades, micro-alloyed steel HX420LAD+Z and dual-phase ferritic–martensitic steel HCT600X+Z, were tested. Each grade underwent five groups of ten samples, which were subjected to identical experimental conditions of local heating by resistance spot welding (RSW) and clinching. The utilization of RSW on the clinched joint region resulted in an average enhancement of 17% in the load-carrying capacity for material HCT600X+Z, and an average increase of 25% for material HX420LAD+Z.

In the present work, the effects of electrolytic hydrogen charging of T92 steel weldments on their room-temperature tensile properties were investigated. Two circumferential weldments between the T92 grade tubes were produced by gas tungsten arc welding using the matching Thermanit MTS 616 filler material. The produced weldments were individually subjected to considerably differing post-welding heat treatment (PWHT) procedures. The first-produced weldment was conventionally tempered (i.e., short-term annealed below the Ac₁ critical transformation temperature of the T92 steel), whereas the second one was subjected to its full renormalization (i.e., appropriate reaustenitization well above the T92 steel Ac₃ critical transformation temperature and subsequent air cooling), followed by its conventional subcritical tempering. From both weldments, cylindrical tensile specimens of cross-weld configuration were machined. The room-temperature tensile tests were performed for the individual welds’ PWHT states in both hydrogen-free and electrolytically hydrogen-charged conditions. The results indicated higher hydrogen embrittlement susceptibility for the renormalized-and-tempered weldments, compared to the conventionally tempered ones. The obtained findings were correlated with performed microstructural and fractographic observations.

The present work is focused on the investigation of isothermal ageing effects on room-temperature tensile properties and the failure of quenched and tempered martensitic/austenitic weldments between T92 and TP316H heat-resistant steels. The dissimilar weldments were produced by gas tungsten arc welding technique using a Ni-based Thermanit Nicro 82 filler metal. The welded joints were subjected to unconventional post-welding heat treatment consisting of the welds solutionizing (1060 °C/30 min), followed by their water quenching and final stabilization tempering (760 °C/60 min). The treatment was completed by spontaneous air cooling within a tempering furnace. The welds in their initial quenched and tempered condition were subsequently aged at 620 °C for up to 2500 h. Apart from room-temperature tensile tests performed for all the welds material states, additional cross-weld hardness measurements were carried out on longitudinal sections of broken tensile specimens. The applied thermal exposure resulted in recognizable deterioration of plastic properties, whereas their effects on strength properties were rather small. The welds tensile straining and fracture evolution exhibited competitive behavior between the austenitic TP316H region and Ni-based weld metal. The observed failure locations showed significant hardness peaks due to intensive, necking-related strain hardening effects occurred during the tensile tests.

The influence of isothermal aging at 620 °C in combination with subsequent electrochemical hydrogen charging at room-temperature was studied on quenched-and-tempered T92/TP316H martensitic/austenitic weldments in terms of their room-temperature tensile properties and fracture behavior. Hydrogen charging of the weldments did not significantly affect their strength properties; however, it resulted in considerable deterioration of their plastic properties along with significant impact on their fracture characteristics and failure localization. The hydrogen embrittlement plays a dominant role in degradation of the plastic properties of the weldments already in their initial material state, i.e., before thermal aging. After thermal aging and subsequent hydrogen charging, mutual superposition of thermal and hydrogen embrittlement phenomena had led to clearly observable effects on the welds deformation and fracture processes. The measure of hydrogen embrittlement was clearly lowered for thermally aged material state, since the contribution of thermal embrittlement to overall degradation of the weldments has dominated. The majority of failures of the weldments after hydrogen charging occurred in the vicinity of T92 BM/Ni weld metal (WM) fusion zone; mostly along the Type-II boundary in Ni-based weld metal. Thus, regardless of aging exposure, the most critical failure regions of the investigated weldments after hydrogen charging and tensile straining at room temperature are the T92 BM/Ni WM fusion boundary and Type-II boundary acting like preferential microstructural sites for hydrogen embrittling effects accumulation.

In this work, solution-annealed AISI 316H grade austenitic stainless steel was studied in terms of investigating the electrolytic hydrogen charging effects on the resulting Charpy impact toughness and dry sliding tribological behavior. Conventional Charpy impact bending tests were employed to study the mechanical response of the investigated material to dynamic loading conditions, whereas dry linear sliding tribological tests were used to study material friction and wear behavior. The obtained mechanical and tribological properties were correlated with corresponding fracture and tribological mechanisms, which were determined from morphological observations of fracture surfaces and tribological tracks. The applied testing procedures were individually carried out for the non-hydrogenated, hydrogen-charged, and dehydrogenated material conditions. The observed changes in individual properties due to applied hydrogen charging were rather small, which indicated the good resistance of solution-annealed AISI 316H steel against material degradation in currently used electrolytic hydrogenation conditions.