The present investigation reports as it is possible to prepared polyvinylidene fluoride (PVDF) membranes for microfiltration (MF) and ultrafiltration (UF) applications, by using triethyl phosphate (TEP) as non–toxic solvent in accordance with the Green Chemistry. Casting solutions containing different concentrations of polyethylene glycol (PEG) were prepared in order to study its effect on the final membrane morphology and properties. The possibility to finely modulate membrane properties was also investigated by applying two different membrane preparation techniques, the Non-Solvent Induced Phase Separation (NIPS) and its coupling with Vapour Induced Phase Separation (VIPS). Membranes’ morphology was detected by Scanning Electron Microscopy (SEM). Thickness, porosity, contact angle, pore size and water permeability were also recorded. Both the PEG content in the dope solution and the selected time intervals during which the nascent films were exposed to established relative humidity and temperature were found to play a crucial role in membrane formation. In particular, it was demonstrated as, by varying PEG content between 10 and 20 wt %, and by setting the exposure time to humidity at 0/2.5/5/7.5 min, membranes with different pore diameter and bicontinuous structure, suitable for UF and MF applications, could be easily obtained.

The approach of the present work is based on the use of poly (methylmethacrylate) (PMMA) polymer, which is compatible with PVDF and TiO₂ nanoparticles in casting solutions, for the preparation of nano-composites membranes using a safer and more compatible solvent. TiO₂ embedded poly (vinylidene fluoride) (PVDF)/PMMA photocatalytic membranes were prepared by phase inversion method. A non-solvent induced phase separation (NIPS) coupled with vapor induced phase separation (VIPS) was used to fabricate flat-sheet membranes using a dope solution consisting of PMMA, PVDF, TiO₂, and triethyl phosphate (TEP) as an alternative non-toxic solvent. Membrane morphology was examined by scanning electron microscopy (SEM). Backscatter electron detector (BSD) mapping was used to monitor the inter-dispersion of TiO₂ in the membrane surface and matrix. The effects of polymer concentration, evaporation time, additives and catalyst amount on the membrane morphology and properties were investigated. Tests on photocatalytic degradation of methylene blue (MB) were also carried out using the membranes entrapped with different concentrations of TiO₂. The results of this study showed that nearly 99% MB removal can be easily achieved by photocatalysis using TiO₂ immobilized on the membrane matrix. Moreover, it was observed that the quantity of TiO₂ plays a significant role in the dye removal.

Lutein has several benefits for human health, playing an important role in the prevention of age-related macular degeneration (AMD), cataracts, amelioration of the first stages of atherosclerosis, and some types of cancer. In this work, the Scenedesmus almeriensis microalga was used as a natural source for the supercritical fluid (SF) extraction of lutein. For this purpose, the optimization of the main parameters affecting the extraction, such as biomass pre-treatment, temperature, pressure, and carbon dioxide (CO₂) flow rate, was performed. In the first stage, the effect of mechanical pre-treatment (diatomaceous earth (DE) and biomass mixing in the range 0.25–1 DE/biomass; grinding speed varying between 0 and 600 rpm, and pre-treatment time changing from 2.5 to 10 min), was evaluated on lutein extraction efficiency. In the second stage, the influence of SF-CO₂ extraction parameters such as pressure (25–55 MPa), temperature (50 and 65 °C), and CO₂ flow rate (7.24 and 14.48 g/min) on lutein recovery and purity was investigated. The results demonstrated that by increasing temperature, pressure, and CO₂ flow rate lutein recovery and purity were improved. The maximum lutein recovery (~98%) with purity of ~34% was achieved operating at 65 °C and 55 MPa with a CO₂ flow rate of 14.48 g/min. Therefore, optimum conditions could be useful in food industries for lutein supplementation in food products.

In this study, Scenedesmus almeriensis as green microalga was cultivated on bench-scale for carbon dioxide (CO₂) capture and lutein production. The autotrophic cultivation of S. almeriensis was carried out by using a vertical bubble column photo-bioreactor (VBC-PBR) with a continuous flow of a gaseous mixture of oxygen (O₂), nitrogen (N₂), and CO₂, the latter in content of 0.0–3.0 %v/v. The liquid phase was batch. S. almeriensis growth was optimized. In addition, lutein extraction was carried out by using accelerated solvent extraction with ethanol as Generally Recognized as Safe (GRAS) solvent at 67 °C and 10 MPa. Upon optimization of CO₂ concentration, the maximum biomass productivity, equal to 129.24 mg·L⁻¹·d⁻¹, was achieved during the cultivation by using a content of CO₂ equal to 3.0 %v/v and it allowed to obtain a lutein content of 8.54 mg·g⁻¹, which was 5.6-fold higher in comparison to the analogous process carried out without CO₂ addition. The ion chemical analysis in the growth medium showed that by gradually increasing CO₂ content, the nutrient consumption during the growth phase also increased. This study may be of potential interest for lutein extraction at industrial scale, since it is focused on pigment production from a natural source with a concomitantly CO₂ capture.

Haematococcus pluvialis microalgae is a promising source of astaxanthin, an excellent antioxidant carotenoid. H. pluvialis, as well as other species, could find more extensive applications as healthy food for a variegated carotenoids composition in addition to astaxanthin. Official method has not currently been used for this purpose. The objective of this work was to propose a method to characterize carotenoids in H. pluvialis after the comparison between spectrophotometric and liquid chromatography analysis. In addition, in order to improve the use of astaxanthin in the food industry, thermal stability was investigated. In this context, the effect of temperature at 40–80 °C, over a 16 h storage period was tested on astaxanthin produced by H. pluvialis. A further test was carried out at room temperature (20 °C) for seven days. A decrease in the astaxanthin concentration was observed at all tested temperatures with a decrease >50% of all-trans isomer at 80 °C after 16 h and an increase of 9-cis and 13-cis isomers. In conclusion, the obtained results showed the importance of evaluating the degradation effect of temperature on astaxanthin used as a food additive for a future greater enhancement of this bioproduct in the food field.

This research shows that carbon dioxide supercritical fluid (CO₂-SF) is an emerging technology for the extraction of high interest compounds for applications in the manufacturing of pharmaceuticals, nutraceuticals, and cosmetics from microalgae. The purpose of this study is to recover fatty acids (FAs) and, more precisely, eicosapentaenoic acid (EPA) from Nannochloropsis gaditana biomass by CO₂-SF extraction. In the paper, the effect of mechanical pre-treatment was evaluated with the aim of increasing FAs recovery. Extraction was performed at a pressure range of 250–550 bars and a CO₂ flow rate of 7.24 and 14.48 g/min, while temperature was fixed at 50 or 65 °C. The effect of these parameters on the extraction yield was assessed at each extraction cycle, 20 min each, for a total extraction time of 100 min. Furthermore, the effect of biomass loading on EPA recovery was evaluated. The highest EPA extraction yield, i.e., 11.50 mg/g, corresponding to 27.4% EPA recovery, was obtained at 65 °C and 250 bars with a CO₂ flow rate of 7.24 g/min and 1.0 g biomass loading. The increased CO₂ flow rate from 7.24 to 14.48 g/min enhanced the cumulative EPA recovery at 250 bars. The purity of EPA could be improved by biomass loading of 2.01 g, even if recovery was reduced.