The aim was to synthesize and characterize an adhesive incorporating HA and GO nanoparticles. Techniques including scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX), micro-tensile bond strength (μTBS), and micro-Raman spectroscopy were employed to investigate bond durability, presence of nanoparticles inside adhesive, and dentin interaction. Control experimental adhesive (CEA) was synthesized with 5 wt% HA. GO particles were fabricated and added to CEA at 0.5 wt% (HA-GO-0.5%) and 2 wt% GO (HA-GO-2%). Teeth were prepared to produce bonded specimens using the three adhesive bonding agents for assessment of μTBS, with and without thermocycling (TC). The adhesives were applied twice on the dentin with a micro-brush followed by air thinning and photo-polymerization. The HA and GO nanoparticles demonstrated uniform dispersion inside adhesive. Resin tags with varying depths were observed on SEM micrographs. The EDX mapping revealed the presence of carbon (C), calcium (Ca), and phosphorus (P) in the two GO adhesives. For both TC and NTC samples, HA-GO-2% had higher μTBS and durability, followed by HA-GO-0.5%. The representative micro-Raman spectra demonstrated D and G bands for nano-GO particles containing adhesives. HA-GO-2% group demonstrated uniform diffusion in adhesive, higher μTBS, adequate durability, and comparable resin tag development to controls.

Hydroxyapatite (HA) delivery with resin adhesives has potential for re-mineralization of resin–dentin interface. The study prepared an adhesive containing HA and confirmed its presence in adhesive and interaction with the dentin using scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), and Micro-Raman spectroscopy. The aim was to assess the influence of HA incorporation in dentin adhesive on its microtensile bond strength (μ-tbs) and Knoop microhardness (KHN). Thirty teeth each were bonded with CA and HA adhesive using a 10-s smear and photo-polymerized. The specimens in each adhesive group (CA and HA) were divided into sub-groups of 24 h, 8 weeks, and 16 weeks (n = 10) aging durations. μ-tbs was assessed at a crosshead speed of 0.5 mm/minute and bonded interface was analyzed using SEM (n = 20) and Raman spectroscopy (n = 10). Softening of HA adhesive and CA was assessed using KHN. HA adhesive presented higher μ-tbs compared to CA. With an increase in storage time, HA adhesive presented with 100% adhesive failure. Softening was less and KHN was higher for HA adhesive compared to CA (p < 0.05). KHN reduction was higher in CA [19.6 (5.1)%] compared to the HA adhesives [9.7 (4.5)%]. HA adhesive showed superior μTBS and microhardness compared to CA. In the absence of nanoleakage, HA modified adhesive exhibited enhanced bond integrity and better durability of resin dentin bond compared to control adhesive.

Dental radiography is widely used in dental practices and offers a valuable resource for the development of AI technology. Consequently, many researchers have been drawn to explore its application in different areas. The current systematic review was undertaken to critically appraise developments and performance of artificial intelligence (AI) models designed for tooth numbering and detection using dento-maxillofacial radiographic images. In order to maintain the integrity of their methodology, the authors of this systematic review followed the diagnostic test accuracy criteria outlined in PRISMA-DTA. Electronic search was done by navigating through various databases such as PubMed, Scopus, Embase, Cochrane, Web of Science, Google Scholar, and the Saudi Digital Library for the articles published from 2018 to 2023. Sixteen articles that met the inclusion exclusion criteria were subjected to risk of bias assessment using QUADAS-2 and certainty of evidence was assessed using GRADE approach.AI technology has been mainly applied for automated tooth detection and numbering, to detect teeth in CBCT images, to identify dental treatment patterns and approaches. The AI models utilised in the studies included exhibited a highest precision of 99.4% for tooth detection and 98% for tooth numbering. The use of AI as a supplementary diagnostic tool in the field of dental radiology holds great potential.

Background: Silane-containing universal adhesives (UAs) are marketed as adhesion promotors for glass-ceramics. Objectives: This study aimed to evaluate the priming capacity of γ-methacryloxypropyltrimethoxysilane (γMPTS)-containing and γ-methacryloxypropyltriethoxysilane (γMPTES)/3-(aminopropyl)triethoxysilane (APTES)-containing universal adhesives (UAs) for lithium disilicate ceramic (LDC). Materials and Methods: Etched LDC discs were distributed into four groups according to the priming material used: (control), no priming; (MBN), LDC was primed with a universal primer (Monobond N); (SBU), γMPTS-containing UA (Single Bond Universal Adhesive) was used as a primer; and (SBP), γMPTES/APTES-containing UA (Scotchbond Universal Plus Adhesive) was used as a primer. LDC discs were cemented using a dual-cure resin cement, then sectioned into microbeams for microtensile bond strength (μTBS) evaluation. Failure modes were assessed. Results: MBN application showed the highest μTBS among all groups. γMPTES/APTES-containing UA (SBP) resulted in considerably higher μTBS compared with γMPTS-containing UA (SBU) or the control group. The mixed failures were the most predominant among all groups. Conclusions: The effect of silane-containing UAs on resin-ceramic μTBS is material dependent. Although γMPTES/APTES-containing UA improved bonding to LDC, the priming of LDC with either of the UAs tested cannot be considered as an alternative to a separate silanization (priming) step using a universal primer.

Dental laboratories (LABs) are integral to the performance of a dentist in providing successful oral rehabilitation. The aim of this study was to compare the adaptation, contour, contacts, and shade matching of different government and commercial dental LABs in the fabrication of porcelain fused to metal (PFM) crowns. Thirty-two dental LABs were selected to fabricate PFM crowns (one PFM crown each). Marginal adaptation, contour, proximal contacts, and shade matching were evaluated. Evaluation of the crowns’ quality was performed following modified USPHS/FDI criteria. Visual and colorimeter assessments were employed to evaluate shade matching. Differences between groups were examined by Pearson’s Chi-square and Fisher’s exact test. The quality of marginal adaptation of crowns was good in 81.25%, however the quality of contours, contacts, and shade matching was compromised in 43.75%, 59.38%, and 39% of all LABs, respectively. Visual and colorimeter shade matching was acceptable in 62.5% and 80% of LABs in the cervical third and middle third regions of crowns, respectively, however in the incisal third the shade matching was unacceptable in nearly 60% of LABs. Commercial laboratories showed significantly better contours and shade matching, but not marginal adaptation. However, no significant differences were found in comparison of proximal contacts between the groups.

This in vitro study investigated the extrinsic tooth-whitening effect of bleaching products containing polyphosphates on the dental enamel surface compared to 10% carbamide peroxide (CP). Eighty human molars were randomly allocated into four whitening-products groups. Group A (control) was treated with 10% CP (Opalescence). The other groups with non-CP over-the-counter (OTC) products were group B = polyphosphates (iWhiteWhitening-Kit); group C = polyphosphates+fluoride (iWhite-toothpaste); and group D = sodium bicarbonate (24K-Whitening-Pen). L*, a*, b* color-parameters were spectrophotometer-recorded at baseline (T0), one day (T1), and one month (T2) post-treatment. Changes in teeth color (ΔE_ab) were calculated. Data were analyzed using ANOVA and the Bonferroni test (α = 0.05). Groups A, B, and D showed significant differences in ΔL*&Δa* parameters at T1, but not in Δb* at T0. Group C showed no difference for ΔL*, Δa*, Δb* at T0 and T1. Group A showed differences for ΔL*, Δa*, Δb*, at T2, while groups B, C, and D had no difference in any parameters at T0. At T1, ΔE_ab values = A > D> B > C (ΔE_ab = 13.4 > 2.4 > 2.1 > 1.2). At T2, ΔE_ab values increased = A > B > C > D (ΔE_ab = 12.2 > 10.6 > 9.2 > 2.4). In conclusion, the 10% CP and Biomimetic polyphosphate extrinsic whitening kit demonstrated the highest color change, while simulated brushing with dark stain toothpaste and a whitening pen demonstrated the lowest color change at both measurement intervals.