Coatings with a thickness from ~40 to ~50 µm on Ti6Al4V titanium alloys were formed by plasma electrolytic oxidation (PEO) in a silicate-hypophosphite electrolyte with the addition of graphene oxide. The PEO treatment was carried out in the anode–cathode mode (50 Hz) at a ratio of anode and cathode currents of 1:1; their sum density was 20 A/dm², and the treatment’s duration was 30 min. The effect of the graphene oxide’s concentration in the electrolyte on the thickness, roughness, hardness, surface morphology, structure, composition, and tribological characteristics of the PEO coatings was studied. Wear experiments, under dry conditions, were carried out in a ball-on-disk tribotester with an applied load of 5 N, a sliding speed of 0.1 m·s⁻¹, and a sliding distance of 1000 m. According to the obtained results, the addition of graphene oxide (GO) into the base silicate-hypophosphite electrolyte leads to a slight decrease in the coefficient of friction (from 0.73 to 0.69) and a reduction in the wear rate by more than 1.5 times (from 8.04 to 5.2 mm³/N·m), with an increase in the GO’s concentration from 0 to 0.5 kg/m³, respectively. This occurs due to the formation of a GO-containing lubricating tribolayer upon contact with the coating of the counter-body in the friction pair. Delamination of the coatings during wear occurs due to contact fatigue; with an increase in the concentration of GO in the electrolyte from 0 to 0.5 kg/m³, this process slows down by more than four times.

Coatings with a thickness from ~40 to ~50 µm on Ti6Al4V titanium alloy were formed by micro-arc oxidation in a silicate-hypophosphite electrolyte with additions of graphene oxide. Micro-arc oxidation treatment was carried out in the anode–cathode mode (50 Hz) with a ratio of anode to cathode currents of 1:1, a total density of 20 A/dm², and a treatment duration of 30 min. The effect of the graphene oxide concentration in electrolytes on the thickness, roughness, hardness, surface morphology, structure, composition of micro-arc oxidation coatings, and its electrochemical corrosion behavior in 3.5% NaCl solution was studied. The input of graphene oxide additives into the base silicate hypophosphite electrolyte led to an increase in the hardness of micro-arc oxidation coatings. Electrochemical polarization studies and impedance data showed that the best characteristics in terms of corrosion-protective ability among coatings formed in electrolytes with graphene oxide additives were those formed in the electrolyte with a graphene oxide concentration of 0.1 g·L^−l. A further increase in the graphene oxide concentration in the electrolyte did not improve the protective properties of micro-arc oxidation coatings.

Aim: The present paper aims to systematize data concerning the prevalence and risk of dental erosion (DE) in adult patients with gastroesophageal reflux disease (GERD) compared to controls. Materials and methods: Core electronic databases, i.e., MEDLINE/PubMed, EMBASE, Cochrane, Google Scholar, and the Russian Science Citation Index (RSCI), were searched for studies assessing the prevalence and risk of DE in adult GERD patients with publication dates ranging from 1 January 1985 to 20 January 2022. Publications with detailed descriptive statistics (the total sample size of patients with GERD, the total sample size of controls (if available), the number of patients with DE in the sample of GERD patients, the number of patients with DE in the controls (if available)) were selected for the final analysis. Results: The final analysis included 28 studies involving 4379 people (2309 GERD patients and 2070 control subjects). The pooled prevalence of DE was 51.524% (95 CI: 39.742–63.221) in GERD patients and 21.351% (95 CI: 9.234–36.807) in controls. An association was found between the presence of DE and GERD using the random-effects model (OR 5.000, 95% CI: 2.995–8.345; I² = 79.78%) compared with controls. When analyzing studies that only used validated instrumental methods for diagnosing GERD, alongside validated DE criteria (studies that did not specify the methodologies used were excluded), a significant association between the presence of DE and GERD was revealed (OR 5.586, 95% CI: 2.311–13.503; I² = 85.14%). Conclusion: The meta-analysis demonstrated that DE is quite often associated with GERD and is observed in about half of patients with this extremely common disease of the upper gastrointestinal tract.

The materials used in dentistry for the fabrication of all-ceramic restorations have undergone great and rapid developments over the last two decades. Among the most common ceramic materials in dentistry are those based on zirconium and lithium disilicate. Due to the properties of these materials, they are in great demand in the field of dental restoration production. Thus, dental restorations that will use those materials are commonly machined in CAD/CAM systems, which offer the possibility of manufacturing all-ceramic dental restorations in a very short period of time. This article reviews the modern materials in the field of all-ceramic dental restorations, their manufacturing processes, as well as what determines which ceramic materials are used for the production of CAD/CAM blanks and their production technology.

This paper presents a study of Al₂O₃–ZrO₂ (ZTA) nanocomposites with different contents of reduced graphene oxide (rGO). The influence of the rGO content on the physico-mechanical properties of the oxide composite was revealed. Graphene oxide was obtained using a modified Hummers method. Well-dispersed ZTA-GO nanopowders were produced using the colloidal processing method. Using spark plasma sintering technology (SPS), theoretically dense composites were obtained, which also reduced GO during SPS. The microstructure, phase composition, and physico-mechanical properties of the sintered composites were studied. The sintered ZTA composite with an in situ reduced graphene content of 0.28 wt.% after the characterization showed improved mechanical properties: bending strength was 876 ± 43 MPa, fracture toughness—6.8 ± 0.3 MPa·m^1/2 and hardness—17.6 ± 0.3 GPa. Microstructure studies showed a uniform zirconia distribution in the ZTA ceramics. The study of the electrical conductivity of reduced graphene oxide-containing composites showed electrical conductivity above the percolation threshold with a small content of graphene oxide (0.28 wt.%). This electrical conductivity makes it possible to produce sintered ceramics by electrical discharge machining (EDM), which significantly reduces the cost of manufacturing complex-shaped products. Besides improved mechanical properties and EDM machinability, 0.28 wt.% rGO composites demonstrated high resistance to hydrothermal degradation.

Coatings with a thickness from 27 to 62 µm on electron beam melted Ti-6Al-4V have been formed by micro-arc oxidation (MAO) in a silicate-hypophosphite electrolyte. MAO tests in the anode-cathode mode (50 Hz) with an anode-to-cathode current ratio of 1:1 and sum current densities 10 and 20 A/dm² were carried out. The duration of the MAO treatment was 30 and 60 min. The effect of the processing parameters on the structural properties of the MAO treated coatings was studied. The current density and treatment time significantly affect the coating thickness and surface roughness. The values of these characteristics increase as the current density increases. The effect of thermal cycling tests on surface morphology, thickness and roughness, and elemental and phase composition of MAO coatings was analyzed. After 50 cycles of thermal cycling from +200 °C to −50 °C, no cracking or delamination of coatings was observed. Coatings formed in 30 min at a current density of 20 A/dm² turned out to be the best in terms of such indicators as surface morphology, thickness, and roughness.