Geopolymers are zeolites like structures based on hydrated aluminosilicates units of SiO₄ and AlO₄. These units, known as poly(sialate), poly(sialate)-siloxo or poly(sialate)-disiloxo are chemically balanced by the group I cations of K⁺, Li⁺, or Na⁺. Simultaneously, the chemical reaction of formation, known as geopolymerization, governs the orientation of the unit, generating mesoporous structures. Multiple methods can be used for pore structure and porosity characterization. Among them, nuclear magnetic resonance (NMR) relaxometry allows the detection of the porous structure in a completely nonperturbative manner. NMR relaxometry may be used to monitor the relaxation of protons belonging to the liquid molecules confined inside the porous structure and, thus, to get access to the pore size distribution. This monitoring can take place even during the polymerization process. The present study implements transverse relaxation measurements to monitor the influence introduced by the curing time on the residual liquid phase of geopolymers prepared with two different types of reinforcing particles. According to our results, the obtained geopolymers contain three types of pores formed by the arrangement of the OH⁻ and Si groups (Si-OH), Si-O-Si groups, Si-O-Al groups, and Si-O rings. After 48 days, the samples cured for 8 h show a high percentage of all three types of pores, however, by increasing the curing time and the percentage of reinforcing particle, the percent of pores decrease, especially, the gel pores.

Global industrialization generates large amount of waste which strongly affects the depositing areas and the living creatures from the surroundings. In the same time, the construction sector meets an exponential development process, resulting in materials and construction areas increase. Therefore, the need of new materials was felt worldwide. One solution that knew a rapid development, especially in this sector, was to obtain new eco-friendly materials through a mechanism called geopolymerization. True this powerful chemical reaction between a waste, rich in aluminum and silicon, and a strong alkaline solution, a tetragonal structure of Al-O-Si is obtained that possess properties comparable to those of Portland cement-based concrete. In the present paper the effect of aggregates on local fly ash based geopolymers is analyzed from the structure and mechanical properties point of view. According to this study, the aggregates strongly influence the density, compression strength and flexural strength at any age of samples.

Natural zeolite is a honeycomb-structured aluminosilicate mineral with an open crystalline structure which makes it suitable for a variety of applications. Given the beneficial effects of zeolites on the properties of cementitious materials, the present paper aims to summarize the recent findings reported in the scientific literature on the use of zeolites in cement-based construction materials. This paper limits the analysis to natural zeolites. The influence of natural zeolites on the workability and setting time of cement-based construction materials revealed that increasing the zeolite content led to a reduction in workability compared to the control mixes. At the same time, the initial and final setting times of cement pastes showed a decreasing trend with an increase in the replacement percentage. The slow pozzolanic reaction of clinoptilolite zeolite results in lower flexural strength and compressive strength values of mortars at the age of 28 days. Blending zeolites with other supplementary cementitious materials resulted in improved values of the mechanical properties of mortar and concrete. The findings regarding the impact of zeolite on the durability of concrete suggest that zeolite shows promise as a viable alternative to cement, with positive effects on various aspects of durability. The majority of the durability factors are interconnected. The presence of conflicting findings is particularly significant in this context, highlighting the need for a comprehensive approach to address these challenges in the future.

This paper describes an experimental investigation into the properties of ambient cured one-part alkali-activated materials (AAMs). Mixes incorporating waste glass (WG), ground granulated blast-furnace slag (GGBS), fly ash (FA), and sodium metasilicate pentahydrate were assessed in terms of workability, water absorption, physical and mechanical properties, and environmental impact. Microstructure investigations on selected mixes were also carried out. The GGBS-only mixes had low workability and high early strength that declined over time, whereas FA-only mixes had virtually no strength. Equal proportions of WG and GGBS provided similar fresh properties to those of GGBS mixes yet comparatively higher strengths and a positive strength time gradient. Mixes incorporating 50% GGBS, 25% FA, and 25% WG had the best balance between mechanical properties and workability, with compressive strengths above 40 MPa suitable for structural applications. An increase in activator content from 14% to 21% enhanced the strengths by 39.1%–54.6%. The flexural strengths were largely proportional to the compressive strengths, the water absorption properties were like those of cement mortars, and dry densities depended on the proportions of the constituent binders. Finally, the AAM mixes had between 53% and 72% less embodied carbon compared with a corresponding cement mortar.

The present work investigates the effect of freeze–thaw cycles on the porosity of three mixtures of road concrete containing blast furnace slag in comparison with two mixtures made with conventional materials. The main technique used in our investigations is nuclear magnetic resonance (NMR) relaxometry. This permitted the extraction of information with respect to the freeze–thaw effect on pore-size distribution, which influences both the mechanical strength and the molecular transport through the material. Moreover, by using this technique, the structure of the air voids was analyzed for the entire pore system in the cement paste and the aggregate particles. The samples under study were first dried in a vacuum oven and then saturated with water or cyclohexane where the distribution of the transverse relaxation times of the protons was recorded. The NMR relaxation measurements were performed on samples extracted from specimens maintained at 300 freeze–thaw cycles and on control samples extracted from specimens kept in water during the freeze–thaw period. Scanning Electron Microscopy (SEM) was used to analyze the microstructure of concrete samples in order to obtain information about the pore sizes and the distance between them. The results from the NMR relaxation measurements were consistent with those obtained by using standard techniques for determining the porosity and the freeze–thaw resistances. The investigations made it possible to establish the optimal composition of blast furnace slag that can be incorporated into road concrete compositions. This non-invasive technique can also complete standard techniques for assessing the porosity and the progress of internal cracks during the freeze–thaw test.