High performances of thermosets deriving from their covalent intermolecular cross-link bonds result in their low recyclability hindering the full exploitation of a truly circular approach for cured thermosets. In this experimental work, the recyclability of a bio-based fully recyclable epoxy resin using a mild chemical recycling process was demonstrated. The recycled polymer obtained was fully characterized to ascertain its structure and properties. MALDI (Matrix-Assisted Laser Desorption/Ionization), GPC (Gel Permeation Chromatography) and NMR (Nuclear Magnetic Resonance) spectroscopy to determine the chemical structure of the recycled polymer were used. The thermomechanical properties of the cured virgin network and of the recycled product obtained were measured by DSC (Differential Scanning Calorimetry) and DMA (Dynamic Mechanical Analysis). Thermogravimetric analysis of the recycled polymer was also performed. The recycled polymer was transformed into a polyurethane by reacting it with an isocyanate. The synthetized polyurethane obtained therefrom was thoroughly characterized by thermogravimetric analysis. This approach proved the possibility to up-scale the recycled product making it available for novel applications exploiting its re-use.

In this work, a novel approach to realize a plasmonic sensor is presented. The proposed optical sensor device is designed, manufactured, and experimentally tested. Two photo-curable resins are used to 3D print a surface plasmon resonance (SPR) sensor. Both numerical and experimental analyses are presented in the paper. The numerical and experimental results confirm that the 3D printed SPR sensor presents performances, in term of figure of merit (FOM), very similar to other SPR sensors made using plastic optical fibers (POFs). For the 3D printed sensor, the measured FOM is 13.6 versus 13.4 for the SPR-POF configuration. The cost analysis shows that the 3D printed SPR sensor can be manufactured at low cost (∼15 €) that is competitive with traditional sensors. The approach presented here allows to realize an innovative SPR sensor showing low-cost, 3D-printing manufacturing free design and the feasibility to be integrated with other optical devices on the same plastic planar support, thus opening undisclosed future for the optical sensor systems.

Organic wastes represent an increasing pollution problem due to the exponential growth of their presence in the waste stream. Among these, waste flour cannot be easily reused by transforming it into high-value-added products. Another major problem is represented by epoxy-based thermosets, which have wide use but also poor recyclability. The object of the present paper is, therefore, to analyze both of these problems and come up with innovative solutions. Indeed, we propose a completely new approach, aimed at reusing the organic waste flour, by converting it into high-value epoxy-based thermosets that could be fully recycled into a reusable plastic matrix when added to the waste epoxy-based thermosets. Throughout the research activity, the organic waste was transformed into an epoxidized prepolymer, which was then mixed with a bio-based monomer cured with a cleavable ammine. The latter reactant was based on Recyclamine™ by Connora Technologies, and in this paper, we demonstrate that this original approach could work with the synthetized epoxy prepolymers derived from the waste flour. The cured epoxies were fully characterized in terms of their thermal, rheological, and flexural properties. The results obtained showed optimal recyclability of the new resin developed.

The present study details the composite fabrication, characterization, and full recyclability of the biobased polymer resins with flax fiber as the reinforcement. Two different biobased resins are selected by varying the resin hardener combination and curing parameters for the comparison. The optimum parameters for the composite preparation are finalized by evaluating the neat resin's mechanical and glass transition temperature (T_g) values. According to the results obtained, a biobased epoxy resin cured by a cleavable hardener displayed the highest T_g (i.e., 93.5°C) upon a two‐step cure cycle, guaranteeing full recyclability. Subsequently, eco‐composite flat panels are manufactured using the selected formulation reinforced with commercial flax‐based fabric. These panel's flexural strength, modulus, and interlaminar shear strength are measured after each curing step. The recyclability yield of the composite is tested, through a specific chemical process, demonstrating the possibility of separating and recovering both the constituent fibers and resin from the composite panels.

This work describes the evaluation of different interlaminar veils to improve the toughening of epoxy/carbon fiber composites manufactured by resin infusion. Three commercial veils have been used in the study: two electro spun thermoplastic nanofiber (Xantulayr^® from Revolution Fibres) with different areal weight, and one micro carbon fibers veil (Optiveil^® from TFP). Two laboratory made veils were also manufactured by electrospinning commercial polyethersulfone (PES) tougheners (Virantage by Solvay). The veils were selected to be either soluble or non-soluble in the epoxy resin matrix during curing. The solubility was analyzed by scanning electron microscopy and dynamic mechanical analysis testing on the cured laminates. The fracture energy was evaluated by double cantilever bending (DCB) testing under Mode I loading. The insoluble thermoplastic nanofibers showed the highest toughening efficiency, followed by the soluble nanofiber veils. The carbon fiber based veil showed no toughness improvement.