Numerous phenomena that occur during the process of machine parts’ regeneration have a significant impact on the loss of their working ability. Therefore, the properties of the working surfaces of the teeth flanks of repaired gears were analyzed in this research. The hereditary properties of the gear teeth are expressed by the interdependence of their geometric and physical-mechanical-metallurgical parameters created during the technological operations of regeneration of worn teeth by welding/hard-facing. The hard-facing was executed with three filler metal types, namely: combination Inox 18/8/6 + EDur 600, Castolin 2 and UTP 670. The tested properties included geometrical accuracy, microstructure and microhardness. Evaluation of the executed regeneration procedures was done by comparing the mentioned parameters of the regenerated gears and the new ones. The tested gears were not withdrawn from production due to damage, but they were newly manufactured and intentionally damaged gears, made of the same materials, subjected to the same manufacturing process. In this way, all influences except for the considered filler metal type were eliminated. Based on results of the conducted experiments, it was possible to establish the influence of the filler metal type on the surface characteristics of the regenerated gears’ teeth flanks.

This paper presents the results of voluminous experimental investigations conducted to analyze the influence of the welding procedure on the performance of regenerated gears. Cylindrical spur gears were tested, both newly manufactured and regenerated, in two fundamentally different ways: by hard facing (surfacing) with the “hard” filler metal (DUR 600-IG) and with the “soft” filler metal (EVB2CrMo) with subsequent cementation and quenching. The regeneration procedures were defined and executed, while, subsequently, the microstructure and microhardness of the hard-faced layers were established and measured, followed by checking the durability of the hard-faced teeth flanks. Finally, techno-economic analysis was performed to establish the rationality of the conducted regenerations, i.e., the costs of regenerated and newly manufactured teeth were compared. Based on the results of the conducted investigations, it was possible to establish the influence of the welding type on the performance characteristics (primarily the service life) of the regenerated gears. For individual reparatory hard facing, the procedure with the “hard” filler metal exhibited better characteristics, while for batch reparation of numerous damaged gears, the reparation with the “soft” filler metal, followed by cementation and heat treatment, might be more convenient.

During the process of regeneration of machine parts, certain phenomena occur that have a significant impact on the loss of their working ability. Hereditary properties are expressed by the interdependence of geometric and physical-mechanical-metallurgical parameters of gear teeth created during the technological operations of regeneration of worn teeth by hard-facing. The influence of the type of additional material (electrodes and their combinations) on the tribological characteristics of welded gear teeth was considered, whereby the so-called hard additional materials were applied. Those are the additional materials that give the required surface hardness of the teeth without subsequent thermal or thermochemical treatment. This research did not involve the regeneration of specific worn gears removed from machine systems, but the new gears were made, which were then damaged and then regenerated by hard-facing using the shielded metal arc welding (SMAW) procedure. Thus, all the tested gears were made of the same material, belonged to one batch and were machined on the same machines with the same machining regimes. The tests were performed on samples made of 20MnCr5 steel for cementation, on a tribometer by the “block on disc” method, which was designed to simulate the operating conditions of coupled teeth of concrete gears in the exploitation conditions. Based on the conducted tribological tests, the average coefficients of friction and topography of the surfaces were determined by measuring the wear trace and it was defined which additional materials give the best tribological characteristics of the surfaces of gears regenerated by hard-facing.

Hard-facing as a type of the coating depositing is increasingly used today. Physical-chemical-metallurgical characteristics of contact layers in tribo-mechanical systems depend on the operating conditions and the conditions under which the work surfaces were created. That is the reason the influence of the processing procedures and regime, used in the contact surfaces formation, on development of the wear process of contact elements, is being considered ever more. To determine the influence of the hard-facing technology on characteristics of the gears’ working surfaces, the experimental investigations were performed on samples hard-faced on the steel for cementation, by varying the filler metals (FM) and the hard-facing regimes. The samples tested were hard-faced by five “hard” and three “soft” filler metals. Experimental investigations included measuring the hard-faced layers’ hardness and determination of their microstructure, as well as the wear resistance in the laboratory conditions, on tribometer and on a specially designed device for tests in the real operating conditions of gears. The wear intensity was monitored by the wear trace’s width in the laboratory conditions and by the share of the teeth surfaces affected by the destructive pitting in the operating conditions. The results obtained were compared to results of the base metal (BM) tests, which provided the certain conclusions on which filler metal and which welding procedure are the optimal ones for regeneration of the worn teeth surfaces.

This work examines how different welding regimes and filler metal types influence the characteristics of hardfaced layers and the associated heat-affected zones (HAZ) in components made of low-alloy steel 30CrMoV9. Bead-on-plate welding tests were carried out on plate specimens, using five filler metals, including four gas-shielded wires with different chemical compositions and one flux-cored wire. For each filler metal, two welding regimes were applied by varying the current, voltage, and travel speed. After welding, the bead geometry and hardness were measured, and bending tests were performed to assess cracking behavior. The results show that both filler metal selection and arc energy have a pronounced effect on bead shape and hardness, as well as on the hardness distribution in the HAZ. It is also observed that, because of the metallurgical characteristics of 30CrMoV9 steel, preheating and/or post-weld heat treatment is required to reduce the risk of cracking. The findings may serve as practical input for process selection and quality control in the fabrication and repair of precision mechanical parts.

Among the numerous artifacts in the scientist's legacy in the Nikola Tesla Museum in Belgrade there are sketches of original conceptual solutions, technical drawings, patent documentation, several sheets of handwritten calculations related to the design of a new fountain model (engine characteristics, fluid flow parameters, dimensions of structural elements), as well as other archival material that testifies to his work on this invention. This research aims to analyze the preserved technical and other archival documents related to the development of several different conceptual solutions of the fountain model for which Tesla, in cooperation with his lawyers, prepared and submitted an application to the Patent Office of the United States of America at the end of October 1913 and for which he was granted US patent No. 1,113,716. We reviewed all the modifications to the construction of the imagined models of the new fountain, which were carried out during the entire development process, from the initial idea to the final patented solutions. To that end, we also made computer models based on original technical and patent documentation.