Highly pure cellulosic polymers obtained from waste lignocellulose offer great potential for designing novel materials in the concept of biorefinery. In this work, alpha-cellulose and nanocrystalline cellulose were isolated from the date palm trunk mesh (DPTM) through a series of physicochemical treatments. Supercritical carbon dioxide treatment was used to remove soluble extractives, and concentrated alkali pretreatment was used to eliminate the lignin portion selectively to obtain alpha-cellulose in approximately 94% yield. Further treatments of this cellulose yielded nanocrystalline cellulose. The structure–property relationship studies were carried out by characterizing the obtained polymers by various standard methods and analytical techniques such as Fourier transform infrared spectroscopy-attenuated total reflection (FTIR-ATR), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), energy dispersive X-ray diffraction (EDX-XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Almost 65% yield of pure cellulose was achieved, out of which 94% is the alpha-cellulose. This cellulose shows good thermal stability and crystallinity. The microscopic analysis of the nanocellulose showed a heterogeneous mix of irregular-shaped particles with a size range of 20–60 nm. The percentage crystallinity of alpha-cellulose and nanocellulose was found to be 68.9 and 71.8, respectively. Thus, this study shows that, this DPTM-based low-cost waste biomass can be a potential source to obtain cellulose and nano-cellulose.

Cellulosic polysaccharides have increasingly been recognized as a viable substitute for the depleting petro-based feedstock due to numerous modification options for obtaining a plethora of bio-based materials. In this study, cellulose triacetate was synthesized from pure cellulose obtained from the waste lignocellulosic part of date palm (Phoenix dactylifera L.). To achieve a degree of substitution (DS) of the hydroxyl group of 2.9, a heterogeneous acetylation reaction was carried out with acetic anhydride as an acetyl donor. The obtained cellulose ester was compared with a commercially available derivative and characterized using various analytical methods. This cellulose triacetate contains approximately 43.9% acetyl and has a molecular weight of 205,102 g·mol⁻¹. The maximum thermal decomposition temperature of acetate was found to be 380 °C, similar to that of a reference sample. Thus, the synthesized ester derivate can be suitable for fabricating biodegradable and “all cellulose” biocomposite systems.

A tremendous potential has been observed in the designing of long afterglow materials for sensing, bioimaging, and encryption applications. In this study, two different strontium aluminate-based luminescent materials; SrAl₂O₄: Eu, Dy (S₁), and Sr₄Al₁₄O₂₅: Eu, Dy (S₂) were melt-mixed with polypropylene (PP) matrix, and the phosphorescence properties were evaluated. After excitation at 320 nm, the PP/S₁ composite exhibited a green emission and the PP/S₂ generated a blue emission at 520 nm and 495 nm, respectively. The emission spectra intensity increased by increasing the content of these luminescent fillers. The attenuated total reflection-Fourier transform infrared (ATR-FTIR) experiments show that no chemical reaction occurred during the melt-mixing process. The differential scanning calorimetry (DSC) results revealed that the total crystallinity of the composites reduced by increasing the amount of the fillers; however, no changes in the temperature of melting (Tm) and crystallization (Tc) of PP were observed. Both fillers improved the impact strength of the composites, but the tensile strength (TS) and modulus (TM) decreased. Poly (ethylene glycol) dimethyl ether (P) plasticizer was used to improve the filler-matrix interaction and its dispersion; nevertheless, it adversely affected the intensity of the luminescence emissions.

This research evaluated the influence of stearic acid, sunflower lecithin, and sorbitan monooleate on soy wax (SYW)/rice bran oil (RBO)-based oleogels. The physiochemical behavior of oleogel samples was evaluated using colorimetry, microscopy, FTIR, mechanical, crystallization kinetics, X-ray diffraction, and a drug release investigation. The prepared oleogels were light yellow, and adding emulsifiers did not change their appearance. All oleogels showed an oil binding capacity of >98%, independent of emulsifier treatment. The surface topography revealed that emulsifiers smoothed the surface of the oleogels. Bright-field and polarized micrographs showed the presence of wax grains and needles. FTIR spectra indicated that oleogel samples had the same functional group diversity as the raw materials. The oleogel samples lacked a hydrogen-bonding peak. Hence, we postulated that non-covalent interactions were involved in the oleogel preparation. According to stress relaxation studies, the firmness and elastic component of oleogels were unaffected by emulsifiers. However, EML3 (oleogel containing sorbitan monooleate) showed lower relaxing characteristics than the others. EML3 exhibited the slowest crystallization profile. Due to its low d-spacing, EML3 was found to have densely packed crystal molecules and the largest crystallite size. The in vitro drug release studies showed that emulsifier-containing oleogels dramatically affected curcumin release. These results may help customize oleogels properties to adjust bioactive component release in the food and pharmaceutical industries.

The aging of polypropylene (PP) composites reinforced with date palm nanofiber (DNF) was investigated in this study in order to predict their long-term performance. To produce composites, date palm nanofibers in the range of 1–5 wt% loading were dry-melt-blended with polypropylene. These biocomposites were then subjected to UV exposure (Xenon arch source) for accelerated weathering for 250 and 500 h according to a standard method. The change in thermal properties before and after accelerated weathering was investigated using thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). TGA analysis shows that the maximum degradation temperature for sample at 1 wt% loading was 382.7 °C, which slightly decreased to 379.9 °C after 250 h and to 367.7 °C after 500 h of weathering. DSC analysis also revealed lower crystallinity of the same samples after exposure to accelerated weathering. Mechanical properties were also studied to identify the damage induced by accelerated weathering. The tensile strength of the highest loading (5 wt%) of the sample was found to occur at 34.83 MPa, which was slightly lowered to 31.64 after 500 h treatment. A minimal decrease in tensile strength, deterioration, and weathering-induced oxidation indicates the excellent stability of these composites. Therefore, our study provides insight into the aging behavior of such composites, which may be useful in dry conditions, as well as nonstructural automotive and other parts for which minimum tensile strength (~25 MPa) is specified.

Conductive plastics are made by placing conductive fillers in polymer matrices. It is known that a conductive filler in a binary polymer blend with a co-continuous morphology is more effective than in a single polymer, because it aids the formation of a ‘segregated conductive network’. We embedded a relatively low-cost conductive filler, aluminium nano platelets, in a 60/40 PBT/PET polymer blend. While 25 vol.% of the Al nanoplatelets when placed in a single polymer (PET) gave a material with the resistivity of an insulator (10¹⁴ Ωcm), the same Al nano platelets in the 60/40 PBT/PET blend reduced the resistivity to 7.2 × 10⁷ Ωcm, which is in the category of an electrostatic charge dissipation material. While PET tends to give amorphous articles, the 60/40 PBT/PET blends crystallised in the time scale of the injection moulding and hence the conductive articles had dimensional stability above the T_g of PET.