In the past few decades, several methods concerning optical thin films have been established to facilitate the development of integrated optics. This paper provides a brief depiction of different techniques for implementing optical waveguide thin films that involve chemical, physical, and refractive index modification methods. Recent advances in these fabrication methods are also been presented. Most of the methods developed for the realization of the thin-films are quite efficient, but they are expensive and require sophisticated equipment. The major interest of the scientists is to develop simple and cost-effective methods for mass production of optical thin films resulting in the effective commercialization of the waveguide technology. Our research group is focused on developing a silica-titania optical waveguide platform via the sol-gel dip-coating method and implementing active and passive optical elements via the wet etching method. We are also exploring the possibility of using nanoimprint lithography (NIL) for patterning these films so that the fabrication process is efficient and economical. The recent developments of this platform are discussed. We believe that silica-titania waveguide technology developed via the sol-gel dip-coating method is highly attractive and economical, such that it can be commercialized for applications such as sensing and optical interconnects.

The bromination of multi-walled carbon nanotubes (MWCNT) was performed with vapor bromine in a closed vessel, and they were subjected to intensive stirring with a magnetic stirrer for up to 14 days. The efficiency of bromination was compared depending upon duration. The structure and surface of the crude and purified products were characterized by detailed physicochemical analyses, such as SEM/EDS, TEM, XRD, TGA, Raman, and XPS spectroscopies. The studies confirmed the presence of bromine covalently bound with nanotubes as well as the formation of inclusion MWCNT–Br₂ complexes. It was confirmed that Br₂ molecules are absorbed on the surface of nanotubes (forming the CNT-Br₂ complex), while they can dissociate close to dangling bonds at CNT defect sites with the formation of covalent C−Br bonds. Thus, any covalent attachment of bromine to the graphitic surface achieved around room temperature is likely related to the defects in the MWCNTs. The best results, i.e., the highest amount of attached Br₂, were obtained for brominated nanotubes brominated for 10 days, with the content of covalently bound bromine being 0.68 at% (by XPS).

The reported work was focused on sol–gel-derived organically modified and fluorinated silica coatings deposited on elastic polymeric foil. The structure and topography of the coatings were tested by infrared spectroscopy and microscopic studies. The functional properties were determined using thermal analysis, surface analysis, and oxygen permeability tests. The barrier feature of the investigated materials against oxygen was correlated with the properties of the coatings. The hybrid (organic–inorganic) structure of the coatings was proven, demonstrating the presence of a silica network modified with alkyl and fluoroalkyl groups since precursors with the isooctyl group or different lengths of the fluoroalkyl chains were used for the syntheses. The coatings were free of defects and had a smooth surface except for the sample containing the longest fluoroalkyl chain (perfluorododecyl group), which showed a wrinkle-like surface. The hydrophobic character of the coatings increased, whereas the oxygen permeation coefficient values decreased (reaching a fourfold lower coefficient in comparison to the bare substrate) with a higher content of the fluorinated carbon atoms in the structure. The results were enriched by the information from the thermomechanical analysis as well as nanoindentation and scratch tests giving values of the glass transition temperature, thermal expansion coefficient, coatings adhesion, and hardness of the investigated systems.

Composite silica-titania waveguide films of refractive index ca. 1.8 are fabricated on glass substrates using a sol-gel method and dip-coating technique. Tetraethyl orthosilicate and tetraethyl orthotitanate with molar ratio 1:1 are precursors. Fabricated waveguides are annealed at 500 °C for 60 min. Their optical properties are studied using ellipsometry and UV-Vis spectrophotometry. Optical losses are determined using the streak method. The material structure and chemical composition, of the silica-titania films are analyzed using transmission electron microscopy (TEM) and electron dispersive spectroscopy (EDS), respectively. The surface morphology was investigated using atomic force microscopy (AFM) and scanning electron microscopy (SEM) methods. The results presented in this work show that the waveguide films are amorphous, and their parameters are stable for over a 13 years. The optical losses depend on their thickness and light polarization. Their lowest values are less than 0.06 dB cm⁻¹. The paper presents the results of theoretical analysis of scattering losses on nanocrystals and pores in the bulk and interfaces of the waveguide film. These results combined with experimental data clearly indicate that light scattering at the interface to a glass substrate is the main source of optical losses. Presented waveguide films are suitable for application in evanescent wave sensors.

A facile procedure for the synthesis of ultra-fine silicon nanoparticles without the need for a Schlenk vacuum line is presented. The process consists of the production of a (HSiO _1.5 ) _n sol–gel precursor based on the polycondensation of low-cost trichlorosilane (HSiCl ₃ ), followed by its annealing and etching. The obtained materials were thoroughly characterized after each preparation step by electron microscopy, Fourier transform and Raman spectroscopy, X-ray dispersion spectroscopy, diffraction methods and photoluminescence spectroscopy. The data confirm the formation of ultra-fine silicon nanoparticles with controllable average diameters between 1 and 5 nm depending on the etching time.