Reinforced steel bars (rebar) are extensively used in construction, and the main challenge is in minimizing corrosion due to oxide or passive layer breakdown. In contrast, dual-phase (DP) steel has good corrosion resistance. This study investigated the effect of Cl⁻ ions on the electrochemical corrosion behavior of DP rebar and conventional rebar. Corrosion behavior studies and electrochemical measurements were conducted on DP rebar and conventional rebar in simulated concrete pore solution with different concentrations of Cl⁻ ions. Microstructure analysis, surface morphology analysis, and corroded surface characterization were performed using optical microscopy, field emission scanning electron microscopy, and Raman spectroscopy, respectively. Potentiodynamic polarization and electrochemical impedance spectroscopy measurements revealed that DP rebar has good passivity, leading to better corrosion resistance and greater strength compared to ordinary rebar. In addition, DP rebar showed better passivity behavior compared to conventional rebar in alkaline solution. Therefore, the presence of a dual phase (ferrite and martensite) in reinforced concrete structured steel induces good corrosion resistance.

Dual-phase (DP) steels consist of a ferritic matrix dispersed with some percentage of martensite, which gives the material a good combination of strength and ductility, along with the capacity to absorb energy and enhanced corrosion protection properties. The purpose of this work was to study the microstructural and corrosion behavior (mainly pitting and galvanic corrosion) of DP steel compared with that of conventional rebar. To obtain DP steel, low-carbon steels were heat-treated at 950 °C for 1 h and then intercritically annealed at 771 °C for 75 min, followed by quenching in ice-brine water. The corrosion rates of DP steel and standard rebar were then measured in different pore solutions. Macro- and microhardness tests were performed for both steels. It was found that DP steels exhibited a superior corrosion resistance and strength compared to standard rebar. The reported results show that DP steels are a good candidate for concrete reinforcement, especially in aggressive and corrosive environments.

The manufacturing of different Ti-6Al-xV (x = 2, 4, 6, and 8 wt.%) alloys using a mechanical alloying technique was reported. The corrosion behaviors of these newly fabricated alloys after 1, 24, and 48 h exposure to a simulated body fluid (SBF) were assessed using cyclic potentiodynamic polarization, electrochemical impedance spectroscopy, and chronoamperometric measurements. Surface morphology and elemental analyses after corrosion for 48 h in SBF were reported using scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) examinations. An X-ray diffraction investigation characterized the phase analyses. All results indicated that the increase of V content significantly decreases both uniform and pitting corrosion. This effect also increases with prolonging the immersion time to 48 h before measurement.

The corrosion behavior of newly fabricated γ-TiAl alloy was studied using electrochemical impedance spectroscopy (EIS) and cyclic potentiodynamic polarization (CPP) techniques. The γ-TiAl alloy was produced from powder with compositions of Ti-48Al-2Cr-2Nb processed using electron beam melting (EBM) technique. The corrosion behavior of the bulk alloy was investigated in 1 M HCl solution for different immersion times and temperatures. The experimental results suggest that the fabricated alloy exhibits good resistance to corrosion in acid solution at room temperature. The results also indicate that with an increase in immersion time and solution temperature, the corrosion potential (Ecorr) shifts to a higher positive value, resulting in an increase in corrosion current (jcorr) and consequently a decrease in the corrosion resistance (Rp) of the alloy.

Owing to their superior biocompatibility, titanium and its alloys are often the first choice for implant materials in biomedical applications, especially for dental and bone repairs (orthodontics and prosthodontics). Titanium has low density and shows good mechanical and chemical properties. Although Ti-6Al-4V alloy exhibits excellent corrosion resistance properties, the metal ions released during corrosion are likely to induce aseptic loosening in long-term implantations. In the present study, Ti-6Al-4V alloy was subjected to two specific heat treatments, namely, air cooling and water quenching. The potentiodynamic polarization and electrochemical impedance spectroscopy measurements revealed remarkable improvement in the corrosion resistance properties of the heat-treated specimens. The presence of the β phase is a plausible reason for the improvement. Scanning electron microscopy, X-ray diffraction phase composition analysis, and microstructural characterization were performed to confirm the presence of the β phase.

The present study investigates the electrochemical corrosion response and tribo-behavior of 304L and 316L stainless steel welded by gas metal arc welding (GMAW), which offered a high deposition rate. During this research, the metallurgically prepared welded samples were subjected to a tribological test and a corrosion test. The wear results were favorable for 316L steel, and it showed a lower coefficient of friction than the 304L specimen. These samples also underwent characterization studies, such as X-ray diffractometry (XRD) and scanning electron microscopy (SEM), to identify the different phases obtained on the cooling of the weld pool. Finally, both specimens were compared against their mechanical properties. Owing to the above properties, the 316L sample showed lasting durability, as compared to the 304L steel. The primary compositional difference is the higher presence of molybdenum and chromium in the 316L steel, compared to the 304L stainless steel.