Gallium nitride (GaN)-based vertical power Schottky barrier diode (SBD) has demonstrated outstanding features in high-frequency and high-power applications. This paper reviews recent progress on GaN-based vertical power SBDs, including the following sections. First, the benchmark for GaN vertical SBDs with different substrates (Si, sapphire, and GaN) are presented. Then, the latest progress in the edge terminal techniques are discussed. Finally, a typical fabrication flow of vertical GaN SBDs is also illustrated briefly.

The optimization of mesa etch for a quasi-vertical gallium nitride (GaN) Schottky barrier diode (SBD) by inductively coupled plasma (ICP) etching was comprehensively investigated in this work, including selection of the etching mask, ICP power, radio frequency (RF) power, ratio of mixed gas, flow rate, and chamber pressure, etc. In particular, the microtrench at the bottom corner of the mesa sidewall was eliminated by a combination of ICP dry etching and tetramethylammonium hydroxide (TMAH) wet treatment. Finally, a highly anisotropic profile of the mesa sidewall was realized by using the optimized etch recipe, and a quasi-vertical GaN SBD was demonstrated, achieving a low reverse current density of 10⁻⁸ A/cm² at −10 V.

The oxygen plasma surface treatment prior to ohmic metal deposition was developed to reduce the ohmic contact resistance (R_C) for AlGaN/GaN high electron mobility transistors (HEMTs) on a high-resistive Si substrate. The oxygen plasma, which was produced by an inductively coupled plasma (ICP) etching system, has been optimized by varying the combination of radio frequency (RF) and ICP power. By using the transmission line method (TLM) measurement, an ohmic contact resistance of 0.34 Ω∙mm and a specific contact resistivity (ρ_C) of 3.29 × 10^–6 Ω∙cm² was obtained with the optimized oxygen plasma conditions (ICP power of 250 W, RF power of 75 W, 0.8 Pa, O₂ flow of 30 cm³/min, 5 min), which was about 74% lower than that of the reference sample. Atomic force microscopy (AFM), energy dispersive X-ray spectroscopy (EDX), and photoluminescence (PL) measurements revealed that a large nitrogen vacancy, which was induced near the surface by the oxygen plasma treatment, was the primary factor in the formation of low ohmic contact. Finally, this plasma treatment has been integrated into the HEMTs process, with a maximum drain saturation current of 0.77 A/mm obtained using gate bias at 2 V on AlGaN/GaN HEMTs. Oxygen plasma treatment is a simple and efficient approach, without the requirement of an additional mask or etch process, and shows promise to improve the Direct Current (DC) and RF performance for AlGaN/GaN HEMTs.

This work investigates the transient characteristics of an AlGaN/GaN lateral Schottky barrier diode (SBD) and its recovery process with a dedicated dynamic measurement system. Both static and dynamic characteristics were measured, analyzed with the consideration of acceptor/donor traps in the C-doped buffer and GaN channel, and verified by Silvaco TCAD (technology computer aided design) simulations. The energy band, electric field, and electron concentration were monitored in the transient simulation to study the origin of the current collapse in the SBD. Using the verified model, the impact of carbon doping concentration in the buffer and the thickness of the unintentionally doped (UID) GaN channel in the transient behavior was estimated. Several observations were revealed. Firstly, the traps in the GaN channel and buffer layer have a significant impact on the current collapse of the device. A severe deterioration of current collapse can be observed in the SBDs with increasing density of acceptor-like traps. Secondly, the current collapse increases with the thinner UID GaN channel layer. This well-performed simulation model shows promise to be utilized for the dynamic performance optimization of GaN lateral devices.

Gallium nitride (GaN) has attracted increased attention because of superior material properties, such as high electron saturation velocity and high electrical field strength, which are promising for high-power microwave applications. We report on a high-performance vertical GaN-based Schottky barrier diode (SBD) and its demonstration in a microwave power limiter for the first time. The fabricated SBD achieved a very low differential specific on-resistance (R_ON,sp) of 0.21 mΩ·cm², attributed to the steep-mesa technology, which assists in reducing the spacing between the edge of the anode and cathode to 2 μm. Meanwhile, a low leakage current of ~10⁻⁹ A/cm²@−10 V, a high forward current density of 9.4 kA/cm² at 3 V in DC, and an ideality factor of 1.04 were achieved. Scattering parameter measurements showed that the insertion loss (S₂₁) was lower than −3 dB until 3 GHz. In addition, a microwave power limiter circuit with two anti-parallel diodes was built and measured on an alumina substrate. The input power level reached 40 dBm (10 watts) in continuous-wave mode at 2 GHz, with a corresponding leakage power of 27.2 dBm (0.5 watts) at the output port of the limiter, exhibiting the great potential of GaN SBD in microwave power limiters.

“Ohmic-before-passivation” process was implemented on ultrathin-barrier AlGaN (<6 nm)/GaN heterostructure to further reduce the ohmic contact resistance $(R_{c})$. In this process, alloyed Ti/AI/Ni/Au ohmic metal was formed first, followed by $\text{AlN}/\text{SiN}_{x}$ passivation contributed to restore two-dimensional electron gas (2DEG) in the access region. Due to the sharp change in the concentration of 2DEG at the metal edge, a reduced transfer length consisted with lower $R_{c}$ are achieved compared to that of ohmic contact on AlGaN (~20 nm)/GaN heterostructure with pre-ohmic recess process. Temperature-dependent current voltage measurements demonstrate that the carrier transport mechanism is dominated by thermionic field emission above 200 K and by field emission below 200 K. The “ohmic-before-passivation” process enables the relative stability of ohmic contacts between 50 K and 475 K and significantly improves the direct current characteristics of GaN-metal-insulator-semiconductor-high electron mobility transistor, offering a promising means for scaling down and enabling the utilization of low-voltage GaN-based power devices in extreme environmental conditions.