Protection against microbiologically influenced corrosion (MIC) is critical for materials used in aquatic environments, as MIC accelerates material degradation and leads to faster structural failure. Copper (Cu) has the potential to substantially improve the MIC resistance in alloys. In this study, high-entropy alloy (HEA) coatings containing Cu were deposited using DC (Direct Current) magnetron sputtering to enhance the corrosion resistance and mechanical properties of various substrates. Two CuCrFeMnNi HEA compositions in the form of bulk alloys and PVD (Physical Vapor Deposition) coatings, with 5% and 10% Cu, were analyzed for their microstructural, mechanical, and anticorrosive characteristics. Deposition parameters were varied to select the optimal values. Microstructural evaluations using SEM-EDS (scanning electron microscopy and energy dispersive X-ray spectroscopy), XRD (X-ray diffraction), and AFM (atomic force microscopy) revealed uniform, dense coatings with good adhesion composed of dendritic and interdendritic BCC (body-centered cubic) and FCC (face centered cubic) structures, respectively. Microhardness tests indicated improved mechanical properties for the samples coated with developed HEAs. The coatings exhibited improved corrosion resistance in NaCl solution, the 10% Cu composition displaying the highest polarization resistance and lowest corrosion rate. These findings suggest that Cu-containing HEA coatings are promising candidates for applications requiring enhanced corrosion protection.

The aim of this paper was to investigate the structure and thermal properties of zirconia ceramics co-doped with rare earth (RE) elements in equimolar concentrations. We prepared (1 − x)ZrO₂ − x(yLa₂O₃ + yNd₂O₃ + ySm₂O₃ + yGd₂O₃ + yYb₂O₃) (x = 0.2; y = 0.2) powders by a hydrothermal method in mild conditions (200 °C, 2 h, 60–100 atm.) The powder was analyzed by XRD, SEM-EDAX, BET, and FT-IR after synthesis and heat treatments at 1200 °C and 1500 °C. The samples exhibit good thermal stability, with a single cubic phase presented after heat treatment at 1500 °C. The compound exhibits a low thermal conductivity (0.61 W·m⁻¹·K⁻¹), a low heat capacity (0.42 J·g⁻¹K⁻¹), and a low thermal diffusivity (0.34 mm²·s⁻¹). The values are lower than reported for conventional RE-doped zirconia.

Materials used in the marine industry are exposed to extreme conditions, so it is necessary to meet remarkable characteristics, such as mechanical resistance, low density, and good corrosion resistance. The challenging environment requires continuous performance improvements, so this work is focused on developing new materials with superior properties, using the electrochemical deposition technique, which are convenient for marine engineering. High-entropy alloys have been attracting tremendous interest in many applications, due to their simple crystal structures and advantageous physical-chemical properties, such as high strength, anti-corrosion, erosion, and electro-magnetic capabilities. To identify the most appropriate compositions, MatCalc software was used to predict the structure and characteristics of the required materials, and thermodynamic and kinetic criteria calculations were performed. The modelling processes generated a series of optimal compositions in the AlCrCuFeNi alloy system, that are suitable to be used in anticorrosive and tribological applications. The composition and morphology of the obtained high entropy alloy thin films revealed a uniform structure, with a small grain profile. The corrosion resistance was investigated in artificial seawater to observe the behavior of the newly developed materials in demanding conditions, and the results showed improved results compared to the copper foil substrate.

In this work, (Ba_0.75Sr_0.25) (Ti_0.95Co_0.05) O₃ perovskite nanostructured material, denoted subsequently as Co-doped BaSrTiO₃, was synthesized in a one-step process in hydrothermal conditions. The obtained powder was heat-treated at 800 °C and 1000 °C, respectively, in order to study nanostructured powder behavior during thermal treatment. The Co-doped BaSrTiO₃ powder was pressed into pellets of 5.08 cm (2 inches) then used for thin film deposition onto commercial Al₂O₃ substrates by RF sputtering method. The microstructural, thermal, and gas sensing properties were investigated. The electrical and thermodynamic characterization allowed the evaluation of thermodynamic stability and the correlation of structural features with the sensing properties revealed under real operating conditions. The sensing behavior with respect to the temperature range between 23 and 400 °C, for a fixed CO₂ concentration of 3000 ppm, highlighted specific differences between Co-doped BaSrTiO₃ treated at 800 °C compared to that treated at 1000 °C. The influence of the relative humidity level on the CO₂ concentrations and the other potential interfering gases was also analyzed. Two possible mechanisms for CO₂ interaction were then proposed. The simple and low-cost technology, together with the high sensitivity when operating at room temperature corresponding to low power consumption, suggests that Co-doped BaSrTiO₃ has a good potential for use in developing portable CO₂ detectors.

The Bi-Sn, Bi-Sn-Ag, and Bi-Sn-Sb solder alloy systems represent lead-free, environmentally friendly alternatives for reliable electronic assembly. These alloys comply with increasingly strict environmental and health regulations, while offering low melting points suitable for soldering temperature-sensitive components. Microstructural analysis revealed distinct phase segregation in all alloys, with Sb promoting coarse Sn₂Sb₃ intermetallic compounds and Ag inducing fine needle-like Ag₃Sn precipitates. Eutectic refinement and compositional contrast were confirmed by SEM-BSE and EDS mapping. Vickers microhardness measurements revealed increased hardness in Sb- and Ag-modified Bi–Sn alloys, with Ag₃Sn dispersion yielding the highest strengthening effect, indicating enhanced mechanical potential. This study also reports the thermal and electrical conductivities of Bi60Sn40, Bi60Sn35Ag5, and Bi60Sn35Sb5 alloys over the 25–140 °C range. Bi60Sn40 showed an increase in thermal conductivity across the full temperature range from 16.93 to 26.93 W/m·K, while Bi60Sn35Ag5 reached 18.28 W/m·K at 25 °C, and Bi60Sn35Sb5 exhibited 13.90 W/m·K. These findings underline the critical influence of alloying elements on microstructure, phase stability, and thermophysical behavior, supporting their application in low-temperature soldering technologies.

Carbon-based materials are promising candidates for enhancing thermal properties of phase change materials (PCMs) without lowering its energy storage capacity. Nowadays, researchers are trying to find a proper porous structure as PCMs support for thermal energy storage applications. In this context, the main novelty of this paper consists in using a ZnO-CNT-based nanocomposite powder, prepared by an own hydrothermal method at high pressure, to obtain porous 3D printed support structures with embedding capacity of PCMs. The morphology of 3D structures, before and after impregnation with three PCMs inorganic salts (NaNO₃, KNO₃ and NaNO₃:KNO₃ mixture (1:1 vol% saturated solution) was investigated by scanning electron microscopy coupled with energy-dispersive X-ray spectroscopy (SEM-EDX). For structure impregnated with nitrates mixture, SEM cross-section morphology suggest that the inorganic salts impregnation started into micropores, continuing with the covering of the 3D structure surface and epitaxial growing of micro/nanostructured crystals, which led to reducing the distance between the structural strands. The variation of melting/crystallization points and associated enthalpies of impregnated PCMs and their stability during five repeated thermal cycles were studied by differential scanning calorimetry (DSC) and simultaneous DSC-thermogravimetry (DSC-TGA). From the second heating-cooling cycle, the 3D structures impregnated with NaNO₃ and NaNO₃-KNO₃ mixture are thermally stable.