New hydrogels films crosslinked with epichlorohydrin were prepared based on alginates and carboxymethyl cellulose with properties that recommend them as potential drug delivery systems (e.g., biocompatibility, low toxicity, non-immunogenicity, hemostatic activity and the ability to absorb large amounts of water). The characterization of their structural, morphological, swelling capacity, loading/release and drug efficiency traits proved that these new hydrogels are promising materials for controlled drug delivery systems. Further, a new theoretical model, in the framework of Scale Relativity Theory, was built with to offer insights on the release process at the microscopic level and to simplify the analysis of the release process.

Ceramic coatings have many advantages for industrial and medical applications due to their exceptional properties. Ceramic coatings with a thickness of approximately 45 μm, after grinding, were grown using a robotic arm that used the atmospheric plasma spraying procedure. The thermal shock stresses—a common situation in applications but difficult to reproduce under laboratory conditions—of the ceramic layers on top of the metal substrate was achieved using solar energy focused by a concentrating mirror, based on experiments conducted in the CNRS-PROMES laboratory, UPR 8521, belonging to the French National Centre for Scientific Research (CNRS). The ceramic layers showed excellent stability at 1000 °C, even at high heating or cooling rates. At high temperatures (above 1800 °C), the exfoliation of the complex ceramic layer was observed. No differences in the structural, phase, mechanical or adhesion properties of the ceramic layer were observed after the thermal shock cycles (in the literature, there have been quite few reports regarding the properties of the ceramic layers after the thermal shock application). Scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), atomic force microscopy (AFM) and X-ray diffraction (XRD) techniques were used to characterize the complex ceramic coating and the effects of thermal shock cycling. The phases and chemical composition of the complex coatings remained similar, insensitive to thermal shock at 1000 °C, consisting of a mixture of crystalline yttrium zirconium oxide and α and γ alumina. For all cases, the main residual stress state was tensile. After 5 or 10 cycles of thermal shocks, a smoothing of the residual stress state was observed in the investigated area. A higher temperature (above 1800 °C), applied as thermal shock, led to higher residual stresses and resulted in large cracks and the spallation of the coating layer.

Ceramic materials as coatings are known to have very good corrosion resistance properties compared to metallic or organic coatings, regardless of environmental conditions. The following samples were used for the experiments: an initial steel substrate and Al₂O₃ + YSZ (12.5%; 25% and 37.5% wt) atmospheric plasma spray-coated samples. The open circuit potential showed similar average values for all samples coated with ceramic layers, which were slightly higher than the potential of the original uncoated sample. The corrosion current densities (i_corr) of all plasma jet sputter-coated systems were very similar and significantly lower than those of the original material. Corrosion rates were much lower in the coated systems due to the chemical inertness of the ceramic coatings, particularly alumina- and zirconia-based coatings. It was observed that ceramic layers improve the corrosion resistance of the metallic material, especially at higher percentages of YSZ in the plasma spray-deposited complex layer. The porosity of the sputter-deposited layers reduced their corrosion resistance due to the contact between the electrolyte solution and the metal substrate created by the interconnection of the pores. The complex equivalent electrical circuit chosen for the analysis of the values led to results in accordance with the experimental parameters.

The aim of this study is to offer a comprehensive view on drug release from hydrogel, from both an experimental and a theoretical point of view. Aiming to benefit cyclodextrins’ properties (not irritant; stable; able to modify the physical, chemical and biological properties of active compounds; accessible at low prices) and those of carrageenan polysaccharide (antitumor, immunomodulatory, antihyperlipidemic, anticoagulant, biocompatibility, biodegradability), original hydrogel films based on beta cyclodextrin and kappa carrageenan using epichlorohydrin as crosslinking agent were prepared and characterized from morphological and physical/chemical points of view. The results (morphology, the swelling degree, and the loading/release capacity) proved their potential as carriers for different types of drugs. Further, a new theoretical model, from a multifractal paradigm of motion, was proposed for the drug release from hydrogel films, starting from the fundaments of its evolution at a microscopic level, and aiming to obtain information on system evolution, at both the spatial and temporal scales, inapproachable by quantitative measurements.